快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PPO Noryl_HMC202M
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP™ STAT-KON™ Compound PPO Noryl_HMC202M
DATA ON BK1005 ONLY.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 980 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 980 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 4.1 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 4.1 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 77300 | kgf/cm² | ASTM D 638 |
| Flexural Stress,brk,1.3mm/min,50mm span | 1380 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 70300 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 86 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 86 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 145 | MPa | ISO 178 |
| Flexural Stress,break,2mm/min | 145 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 7150 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 27 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 4 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 97 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 180 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 177 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 171 | ℃ | ASTM D 648 |
| HDT,0.45 MPa,6.4mm,unannealed | 181 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,6.4mm,unannealed | 173 | ℃ | ASTM D 648 |
| CTE,-30℃ to 30℃,flow | 6.12E-05 | 1/℃ | ASTM D 696 |
| CTE,-30℃ to 30℃,xflow | 1.58E-04 | 1/℃ | ASTM D 696 |
| CTE,23℃ to 150℃,flow | 1.30E-05 | 1/℃ | ISO 11359-2 |
| CTE,23℃ to 150℃,xflow | 5.70E-05 | 1/℃ | ISO 11359-2 |
| Vicat Softening Temp,Rate B/120 | 180 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 177 | ℃ | ISO 75/Af |
| Relative Temp Index,Elec | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 50 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm(5) | 0.1-0.3 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm(5) | 0.4-0.6 | % | SABIC Method |
| Melt Flow Rate,300℃/5.0 kgf | 7.6 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.00E+04 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94V-1 Flame Class Rating(3) | 1.49 | mm | UL 94 |
| Source GMD,last updated:2001/12/14 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 110-120 | ℃ |
| Drying Time | 3-4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300-325 | ℃ |
| Nozzle Temperature | 300-325 | ℃ |
| Front-Zone 3 Temperature | 290-325 | ℃ |
| Middle-Zone 2 Temperature | 275-320 | ℃ |
| Rear-Zone 1 Temperature | 265-315 | ℃ |
| Mold Temperature | 80-110 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 20-100 | rpm |
| Shot to Cylinder Size | 30-70 | % |
| Source GMD,last updated:2001/12/14 | ||