快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PPO HMC3008A 添加30%的玻璃/矿物/碳纤树脂,防静电PPO
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP™ STAT-KON™ Compound PPO Noryl_HMC3008A
LNP* Stat-kon* Noryl_HMC3008A compound is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT. Tight tolerance molding.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 1010 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 1060 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 3 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 4 | % | ASTM D 638 |
| Flexural Stress,yld,2.6mm/min,100mm span | 1300 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,2.6mm/min,100mm span | 100500 | kgf/cm² | ASTM D 790 |
| Hardness,Rockwell R | 120 | - | ASTM D 785 |
| Taber Abrasion,CS-17,1 kg | 77 | mg/1000cy | ASTM D 1044 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 15 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,6.4mm,unannealed | 121 | ℃ | ASTM D 648 |
| Relative Temp Index,Elec | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 50 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.28 | - | ASTM D 792 |
| Water Absorption,24 hours | 0.06 | % | ASTM D 570 |
| Mold Shrinkage,flow,3.2mm(5) | 0.05-0.15 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm(5) | 0.15-0.3 | % | SABIC Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.00E+03 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.00E+05 | Ohm | ASTM D 257 |
| Static Decay,5000V to <50V | 0.01 | < seconds | FTMS101B |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94V-1 Flame Class Rating(3) | 2.48 | mm | UL 94 |
| Oxygen Index(LOI) | 39 | % | ASTM D 2863 |
| Source GMD,last updated:1999/03/15 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 100-105 | ℃ |
| Drying Time | 3-4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270-300 | ℃ |
| Nozzle Temperature | 270-300 | ℃ |
| Front-Zone 3 Temperature | 260-300 | ℃ |
| Middle-Zone 2 Temperature | 250-295 | ℃ |
| Rear-Zone 1 Temperature | 240-290 | ℃ |
| Mold Temperature | 65-95 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 20-100 | rpm |
| Shot to Cylinder Size | 30-70 | % |
| Vent Depth | 0.038-0.051 | mm |