Cycoloy* Resin
When Both Appearance and Durability are Important
Cycoloy Resins are Polycarbonate/Acrylonitrile-Butadiene-Styrene (PC/ABS) high impact amorphous thermoplastic blends that combine ease of processing with low-temperature ductility. This resin family provides excellent heat and impact resistance, as well as outstanding aesthetics. Cycoloy Resin blends offer an excellent design solution when both appearance and durability are important.

Cycoloy* Resin EXCY0025 数据
Recyle Material with PC+ABS+EXL recycle for good low temperature impact performance.

Property
TYPICAL PROPERTIES (1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,yld,Type I,50mm/min	450	kgf/cm²	ASTM D 638
Tensile Stress,brk,Type I,50mm/min	440	kgf/cm²	ASTM D 638
Tensile Strain,brk,Type I,50mm/min	90	%	ASTM D 638
Tensile Modulus,50mm/min	22100	kgf/cm²	ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span	730	kgf/cm²	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	20500	kgf/cm²	ASTM D 790
Tensile Stress,yield,50mm/min	44	MPa	ISO 527
Tensile Strain,yield,50mm/min	4	%	ISO 527
Tensile Strain,break,50mm/min	100	%	ISO 527
Flexural Stress,yield,2mm/min	71	MPa	ISO 178
Flexural Modulus,2mm/min	2000	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact,notched,23℃	70	cm-kgf/cm	ASTM D 256
Izod Impact,notched,-30℃	54	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy,23℃	458	cm-kgf	ASTM D 3763
Instrumented Impact Total Energy,-30℃	458	cm-kgf	ASTM D 3763
Instrumented Impact Total Energy,-40℃	479	cm-kgf	ASTM D 3763
Izod Impact,notched 80*10*4 +23℃	47	kJ/m²	ISO 180/1A
Izod Impact,notched 80*10*4 -30℃	41	kJ/m²	ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm	55	kJ/m²	ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm	44	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
HDT,0.45 MPa,3.2mm,unannealed	119	℃	ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed	98	℃	ASTM D 648
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm	120	℃	ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm	100	℃	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.13	-	ASTM D 792
Melt Flow Rate,260℃/5.0 kgf	9	g/10 min	ASTM D 1238
Density	1.13	g/cm³	ISO 1183
Source GMD,last updated:2004/08/05

Parameter Injection Molding	Value	Unit
Drying Temperature	105-110	℃
Drying Time	3-4	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	275-300	℃
Nozzle Temperature	275-300	℃
Front-Zone 3 Temperature	260-300	℃
Middle-Zone 2 Temperature	255-295	℃
Rear-Zone 1 Temperature	250-290	℃
Mold Temperature	60-90	℃
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	30-80	%
Vent Depth	0.038-0.076	mm
Source GMD,last updated:2004/08/05

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.