Cycoloy* Resin
When Both Appearance and Durability are Important
Cycoloy Resins are Polycarbonate/Acrylonitrile-Butadiene-Styrene (PC/ABS) high impact amorphous thermoplastic blends that combine ease of processing with low-temperature ductility. This resin family provides excellent heat and impact resistance, as well as outstanding aesthetics. Cycoloy Resin blends offer an excellent design solution when both appearance and durability are important.

Cycoloy* Resin C8080REC 数据
PC+ABS Recycle Resin with good flow, good temperature resistance and moderate impact

Property
TYPICAL PROPERTIES (1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,yld,Type I,50mm/min	570	kgf/cm²	ASTM D 638
Tensile Stress,brk,Type I,50mm/min	560	kgf/cm²	ASTM D 638
Tensile Strain,yld,Type I,50mm/min	4.6	%	ASTM D 638
Tensile Strain,brk,Type I,50mm/min	110	%	ASTM D 638
Tensile Modulus,50mm/min	26000	kgf/cm²	ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span	940	kgf/cm²	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	25400	kgf/cm²	ASTM D 790
Tensile Stress,yield,50mm/min	56	MPa	ISO 527
Tensile Stress,break,50mm/min	47	MPa	ISO 527
Tensile Strain,yield,50mm/min	5	%	ISO 527
Tensile Strain,break,50mm/min	85	%	ISO 527
Tensile Modulus,1mm/min	2380	MPa	ISO 527
Flexural Stress,yield,2mm/min	92	MPa	ISO 178
Flexural Modulus,2mm/min	2480	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact,notched,23℃	70	cm-kgf/cm	ASTM D 256
Izod Impact,notched,-30℃	20	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy,23℃	576	cm-kgf	ASTM D 3763
Instrumented Impact Total Energy,-30℃	518	cm-kgf	ASTM D 3763
Instrumented Impact Total Energy,-40℃	541	cm-kgf	ASTM D 3763
Izod Impact,notched 80*10*4 +23℃	51	kJ/m²	ISO 180/1A
Izod Impact,notched 80*10*4 -30℃	17	kJ/m²	ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm	54	kJ/m²	ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm	19	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp,Rate B/50	127	℃	ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed	126	℃	ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed	107	℃	ASTM D 648
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm	129	℃	ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm	113	℃	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.17	-	ASTM D 792
Mold Shrinkage,flow,3.2mm(5)	0.8-1	%	SABIC Method
Mold Shrinkage,xflow,3.2mm(5)	0.8-1	%	SABIC Method
Melt Flow Rate,300℃/1.2 kgf	13	g/10 min	ASTM D 1238
Density	1.17	g/cm³	ISO 1183
Source GMD,last updated:2012/02/24

Parameter Injection Molding	Value	Unit
Drying Temperature	105-110	℃
Drying Time	3-4	hrs
Drying Time(Cumulative)	8	hrs
Maximum Moisture Content	0.04	%
Melt Temperature	275-300	℃
Nozzle Temperature	275-300	℃
Front-Zone 3 Temperature	260-300	℃
Middle-Zone 2 Temperature	255-295	℃
Rear-Zone 1 Temperature	250-290	℃
Mold Temperature	60-90	℃
Back Pressure	0.3-0.7	MPa
Screw Speed	40-70	rpm
Shot to Cylinder Size	30-80	%
Vent Depth	0.038-0.076	mm
Source GMD,last updated:2012/02/24

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.

(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.