- 产 品：PPE PPX7110 耐冲击,耐热好
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Noryl PPX* Resin
Ready for Your Needs
Noryl PPX* resins are modified polyphenylene ether (PPE) / polypropylene (PP) resin blends that offer excellent melt strength and processibility, dimensional stability at temperature extremes, a wide range of stiffness, chemical resistance, and hydrolytic stability. Grades include recyclable unfilled and filled, high elongation, impact modified, and high stiffness.
Noryl PPX* Resin PPE PPX7110 数据表
PPE+PP blend. High Impact, Good Heat Resistance
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 360 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 330 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 6.5 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 195 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 13700 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 520 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 15800 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 44 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 15 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 387 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-30℃ | 283 | cm-kgf | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 138 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 113 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 77 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 8.10E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 1.12E-04 | 1/℃ | ASTM E 831 |
| Relative Temp Index,Elec | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 50 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 0.97 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm(5) | 0.8-1.2 | % | SABIC Method |
| Melt Flow Rate,260℃/5.0 kgf | 10.6 | g/10 min | ASTM D 1238 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94HB Flame Class Rating(3) | 1.52 | mm | UL 94 |
| Source GMD,last updated:2001/02/20 | |||
• No drying is required if extruder is vented. Melt temperature is measurement of the melt exiting the die.
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 60-65 | ℃ |
| Drying Time | 2-4 | hrs |
| Drying Time(Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260-290 | ℃ |
| Nozzle Temperature | 260-290 | ℃ |
| Front-Zone 3 Temperature | 250-290 | ℃ |
| Middle-Zone 2 Temperature | 240-280 | ℃ |
| Rear-Zone 1 Temperature | 225-275 | ℃ |
| Mold Temperature | 30-50 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 20-100 | rpm |
| Shot to Cylinder Size | 30-70 | % |
| Vent Depth | 0.038-0.051 | mm |
| Parameter Sheet Extrusion | Value | Unit |
| Drying Temperature | 60-65 | ℃ |
| Drying Time | 2-4 | hrs |
| Drying Time(Cumulative) | 4 | hrs |
| Melt Temperature | 270-280 | ℃ |
| Barrel-Zone 1 Temperature | 145-155 | ℃ |
| Barrel-Zone 2 Temperature | 255-265 | ℃ |
| Barrel-Zone 3 Temperature | 270-280 | ℃ |
| Barrel-Zone 4 Temperature | 270-280 | ℃ |
| Adapter Temperature | 265-270 | ℃ |
| Die Temperature | 265-270 | ℃ |
| Source GMD,last updated:2001/02/20 | ||
• Melt temperatures below 270℃ (520℉) may result in slight surface texture on thermoformed parts.
• It is recommended that sheet be cured 24 hrs prior to thermoforming.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【Noryl PPX* Resin PPE+PP PPX7110】