PPE PPX7200 改进的耐化学和表面美观级
  • 产 品:PPE PPX7200 改进的耐化学和表面美观级
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Noryl PPX* Resin
Ready for Your Needs
Noryl PPX* resins are modified polyphenylene ether (PPE) / polypropylene (PP) resin blends that offer excellent melt strength and processibility, dimensional stability at temperature extremes, a wide range of stiffness, chemical resistance, and hydrolytic stability. Grades include recyclable unfilled and filled, high elongation, impact modified, and high stiffness.

Noryl PPX* Resin PPX7200 数据表
PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 340 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 280 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 10 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 130 % ASTM D 638
Tensile Modulus,50mm/min 12600 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 490 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 14700 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 34 MPa ISO 527
Tensile Stress,break,50mm/min 28 MPa ISO 527
Tensile Strain,yield,50mm/min 8.2 % ISO 527
Tensile Strain,break,50mm/min 115 % ISO 527
Tensile Modulus,1mm/min 1670 MPa ISO 527
Flexural Stress,yield,2mm/min 48 MPa ISO 178
Flexural Modulus,2mm/min 1600 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 147 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 15 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 0 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 368 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 14 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 8 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 12 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 6 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 80 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 146 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 110 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 71 ASTM D 648
CTE,-40℃ to 40℃,flow 9.90E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 1.08E-04 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 9.90E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 1.08E-04 1/℃ ISO 11359-2
Ball Pressure Test,75℃ +/- 2℃ - - IEC 60695-10-2
Vicat Softening Temp,Rate B/50 103 ISO 306
Vicat Softening Temp,Rate B/120 107 ISO 306
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 73 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 0.99 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.6-0.8 % SABIC Method
Mold Shrinkage,xflow,3.2mm(5) 0.6-0.8 % SABIC Method
Melt Flow Rate,260℃/5.0 kgf 16 g/10 min ASTM D 1238
Density 0.99 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 0.05 % ISO 62
Moisture Absorption(23℃/50% RH) 0.02 % ISO 62
Melt Volume Rate,MVR at 260℃/5.0 kg 18 cm³/10 min ISO 1133
Source GMD,last updated:2006/02/07
Parameter Injection Molding Value Unit
Drying Temperature 60-65
Drying Time 2-4 hrs
Drying Time(Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 260-290
Nozzle Temperature 260-290
Front-Zone 3 Temperature 250-290
Middle-Zone 2 Temperature 240-280
Rear-Zone 1 Temperature 225-275
Mold Temperature 30-50
Back Pressure 0.3-0.7 MPa
Screw Speed 20-100 rpm
Shot to Cylinder Size 30-70 %
Vent Depth 0.038-0.051 mm
Source GMD,last updated:2006/02/07

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.