- 产 品：PA612 FG77G33L NC010 玻纤33%增强,食品级
- 产 地：DuPont 杜邦
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® FG77G33L NC010 is a 33% glass fiber reinforced polyamide 612 resin for injection molding. It has been developed for consideration for applications such as parts in the food industry.
zytel®FG77G33L NC010是一个33%玻璃纤维增强聚酰胺612树脂注塑成型。它已发展为考虑等应用在食品工业。
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA612-GF33
>PA612-GF33<
|
|
|
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Poissons Ratio
Flexural Modulus
Notched Izod Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Izod Impact Strength
-30℃(-22℉)
23℃(73℉)
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 178
ISO 180/1A
ISO 180/1U
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
2
kJ/m
2
kJ/m
|
168(24.4)
3.2
9500(1380)
0.39
8200(1190)
11
11
13
60
70
12
11
13
60
80
|
140(20.3)
3.2
7900(1150)
7000(1015)
10
10
12
45
60
10
10
12
65
90
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Parallel
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
Glass Transition Temperature
10℃/min
Thermal Conductivity
Specific Heat
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 11357-1/-2
ISO 11357-4
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
2
W/m K(Btu in/h ft F)
J/kg K(Btu/lb F)
|
216(421)
200(392)
218(424)
0.26(0.14)
0.17(0.09)
0.16(0.09)
0.83(0.46)
1.13(0.63)
1.58(0.88)
70(158)
0.26(1.8)
2130(0.51)
|
|
|
Other
Density
Water Absorption
Equilibrium 50%RH
Immersion 24h
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
|
1320(1.32)
0.7
0.3
1.8
0.9
0.3
|
|
|
Property
|
Test Method
|
Units
|
Value
|
|
|
DAM
|
50%RH
|
|||
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
280-300(535-570)
290(555)
70-120(160-250)
100(210)
2-4
80(175)
<0.15
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2012