- 产 品：PA612 I1000 未填充,尼612化合物
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP* Colorcomp* Compound
LNP Colorcomp All Series
LNP* Colorcomp* resins contain colorants and special effects for a dazzling spectrum of colored materials. Among the offerings are opaque, translucent, and transparent resins, plus special effects, including edge glow, sparkle, glow, pearlescent, and thermochromic. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™Colorcomp™ Compound PA612 I1000 数据
Also known as:LNP™Colorcomp™Compound I-1000 BK8-114
Product reorder name:I1000
LNP* Colorcomp* I1000 is an unfilled custom colored compound based on Nylon 6/12.
| MECHANICAL | Value | Unit | Standard |
| Tensile Strain,brk,Type I,5mm/min | 100 | % | ASTM D 638 |
| Tensile Stress,yield,5mm/min | 62 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 4.5 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2390 | MPa | ISO 527 |
| THERMAL | Value | Unit | Standard |
| HDT,1.82 MPa,3.2mm,unannealed | 55 | ℃ | ASTM D 648 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 135 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 62 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.06 | - | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 1-3 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1-3 | % | ASTM D 955 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.00E+15 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.00E+12 | Ohm | ASTM D 257 |
| Relative Permittivity,100 Hz | 3.6 | - | ASTM D 150 |
| Relative Permittivity,1 MHz | 3.2 | - | ASTM D 150 |
| Dissipation Factor,100 Hz | 0.02 | - | ASTM D 150 |
| Dissipation Factor,1 kHz | 0.02 | - | ASTM D 150 |
| Dissipation Factor,100 kHz | 0.014 | - | ASTM D 150 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Oxygen Index(LOI) | 27 | % | ISO 4589 |
| Source GMD,last updated:2011/05/06 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12-0.2 | % |
| Melt Temperature | 270-275 | ℃ |
| Front-Zone 3 Temperature | 270-280 | ℃ |
| Middle-Zone 2 Temperature | 260-270 | ℃ |
| Rear-Zone 1 Temperature | 255-265 | ℃ |
| Mold Temperature | 65-95 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2011/05/06 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.PP BJ730 高流动,高冲击树脂
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字：【LNP™Colorcomp™ Compound PA612 I1000】