DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Extrusion Resins
挤出树脂
Zytel® 158 NC010 is an intermediate viscosity PA 612 resin.
zytel®158 NC010是一个中间粘度PA612树脂。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA612
>PA612<
|
|
Mechanical
Yield Stress
Yield Strain
Nominal Strain at Break
Tensile Modulus
Poissons Ratio
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
MPa(kpsi)
2
kJ/m
2
kJ/m
|
62(9)
4.3
35
2400(348)
0.4
4.2
4.2
NB
NB
|
52(7.5)
19
>50
1500(218)
4
8
NB
NB
|
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Parallel
23-55℃(73-130℉)
CLTE, Normal
23-55℃(73-130℉)
Vicat Softening Temperature
50N
|
ISO 75-1/-2
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
ISO 306
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
℃(℉)
|
135(275)
62(144)
218(424)
1.2(0.67)
1.2(0.67)
181(358)
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Electrical
Surface Resistivity
Volume Resistivity
Relative Permittivity
1E2 Hz
1E3 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E3 Hz
1E6 Hz
CTI
|
IEC 60093
IEC 60093
IEC 60250
IEC 60250
UL 746A
|
ohm
ohm m
E-4
V
|
1E12
>1E13
3.6
4.0
3.2
140
200
165
>600
|
1E11
6.0
5.3
4.0
1500
1500
1000
|
Flammability
Flammability Classification
0.86mm
1.5mm
3.0mm
Flammability Classification
0.86mm
1.5mm
3.0mm
Oxygen Index
High Amperage Arc Ignition Resistance
0.86mm
1.5mm
3.0mm
Hot Wire Ignition
0.86mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
UL 746A
UL 746A
|
%
arcs
s
|
HB
HB
HB
HB
HB
HB
25
200
200
200
9
9
19
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Temperature Index
RTI, Electrical
0.86mm
1.5mm
3.0mm
RTI, Impact
0.86mm
1.5mm
3.0mm
RTI, Strength
0.86mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
105
105
105
65
65
65
65
65
65
|
|
Other
Density
Hardness, Rockwell
Scale R
Water Absorption
Equilibrium 50%RH
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 3.2mm(0.125in)
Transverse, 3.2mm(0.125in)
|
ISO 1183
ISO 2039/2
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1060(1.06)
114
1.3
3
1.5
1.5
1.1
1.1
|
108
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Processing-Injection Molding
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
230-290(445-550)
250(480)
50-90(120-190)
70(160)
2-4
80(175)
<0.05
|
|
Processing-Extrusion
Melt Temperature Range
Melt Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
h
℃(℉)
%
|
230-240(445-465)
235(455)
4-6
80(175)
<0.05
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2008