DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Extrusion Resins
挤出树脂
Zytel® 158L NC010 is an intermediate viscosity, lubricated polyamide 612 resin that is suitable for molding and extrusion applications.
zytel®158L NC010是一个中间的粘度,润滑聚酰胺612树脂是适用于成型和挤出应用。
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Identification
Resin Identification
Part Marking Code
|
ISO 1043
ISO 11469
|
|
PA612
>PA612<
|
|
Mechanical
Yield Stress
Nominal Strain at Break
Yield Strain
Tensile Modulus
Flexural Modulus
Notched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
-30℃(-22℉)
23℃(73℉)
|
ISO 527
ISO 527
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
|
MPa(kpsi)
%
%
MPa(kpsi)
MPa(kpsi)
2
kJ/m
2
kJ/m
|
62(9.0)
35
4.5
2400(348)
2050(360)
5
4
NB
NB
|
52(7.5)
>100
19
1500(217)
1450(210)
4
6
NB
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
-30-30℃(-22-86℉)
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
|
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
ISO 11359-1/-2
|
℃(℉)
℃(℉)
E-4/C(E-4/F)
E-4/C(E-4/F)
|
135(275)
62(144)
218(424)
0.9(0.5)
1.2(0.66)
1.8(1.0)
0.9(0.5)
0.9(0.5)
1.2(0.66)
1.7(0.9)
|
|
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Dissipation Factor
1E2 Hz
1E6 Hz
CTI
CTI
3.0mm
|
IEC 60250
IEC 60250
IEC 60112
UL 746A
|
E-4
V
V
|
3.6
3.2
140
160
600
>600
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Flammability
Flammability Classification
0.86mm
1.5mm
3.0mm
Flammability Classification
0.86mm
1.5mm
3.0mm
Oxygen Index
High Amperage Arc Ignition Resistance
0.75mm
1.5mm
3.0mm
Hot Wire Ignition
0.86mm
1.5mm
3.0mm
|
IEC 60695-11-10
UL94
ISO 4589-1/-2
UL 746A
UL 746A
|
%
arcs
s
|
HB
HB
HB
HB
HB
HB
25
200
200
200
9
9
19
|
|
Temperature Index
RTI, Electrical
0.86mm
1.5mm
3.0mm
RTI, Impact
0.86mm
1.5mm
3.0mm
RTI, Strength
0.86mm
1.5mm
3.0mm
|
UL 746B
UL 746B
UL 746B
|
℃
℃
℃
|
105
105
105
65
65
65
65
65
65
|
|
Property
|
Test Method
|
Units
|
Value
|
|
DAM
|
50%RH
|
|||
Other
Density
Water Absorption
Equilibrium 50%RH
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
Mold Shrinkage
Flow, 3.2mm(0.126in)
|
ISO 1183
ISO 62, Similar to
ISO 294-4
|
3 3
kg/m(g/cm )
%
%
%
|
1060(1.06)
1.3
1.4
1.3
1.1
|
|
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
|
|
℃(℉)
℃(℉)
℃(℉)
℃(℉)
h
℃(℉)
%
|
230-290(445-550)
250(480)
50-90(120-190)
70(160)
2-4
80(175)
<0.05
|
|
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm.
Test temperatures are 23℃ unless otherwise stated.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2005.