PA66 LNP* Lubricomp* Compound RBL36L
  • 产 品:PA66 LNP* Lubricomp* Compound RBL36L
  • 产 地:美国LNP
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ Lubricomp™ Compound PA66 RBL36L 塑料数据

Also known as:LNP™ Lubricomp™ Compound RBL-4036 LE
Product reorder name:RBL36L
LNP* Lubricomp* RBL36L is a compound based on Nylon 6/6 containing Glass Beads and PTFE Lubricant. Characteristics of this grade are: Low Extractable.

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 670 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 8.8 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 9.1 % ASTM D 638
Tensile Modulus,5mm/min 42600 kgf/cm² ASTM D 638
Flexural Modulus,1.3mm/min,50mm span 40200 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 58 MPa ISO 527
Tensile Strain,break,5mm/min 8.3 % ISO 527
Tensile Modulus,1mm/min 4100 MPa ISO 527
Flexural Stress 109 MPa ISO 178
Flexural Modulus,2mm/min 3810 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 34 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Multiaxial Impact 15 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 54 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 23 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 231 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 91 ASTM D 648
CTE,-30℃ to 30℃,flow 1.02E+02 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 7.52E+01 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 223 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 97 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.53 - ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.43 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 2-4 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1-3 % ASTM D 955
Wear Factor Washer 32 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 0 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.57 - ASTM D 3702 Modified
Static COF 0.58 - ASTM D 3702 Modified
Density 1.52 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.54 % ISO 62
Source GMD,last updated:2012/08/29
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD, last updated:2012/08/29

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.