Also known as:LNP* Lubricomp* Compound RA-1004 |
Product reorder name:RA004 |
LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing Aramid. Added features of this material include: Internally Lubricated.
|
Property
|
TYPICAL PROPERTIES (1) | ||||
MECHANICAL
|
Value | Unit | Standard | |
Tensile Stress, break
|
890
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Strain, break
|
4.5
|
%
|
ASTM D 638
|
|
Flexural Stress
|
1400
|
kgf/cm²
|
ASTM D 790
|
|
Flexural Modulus
|
44900
|
kgf/cm²
|
ASTM D 790
|
|
IMPACT
|
Value | Unit | Standard | |
Izod Impact, unnotched, 23°C
|
37
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
3
|
cm-kgf/cm
|
ASTM D 256
|
|
THERMAL
|
Value | Unit | Standard | |
HDT, 1.82 MPa, 3.2mm, unannealed
|
171
|
°C
|
ASTM D 648
|
|
PHYSICAL
|
Value | Unit | Standard | |
Density
|
1.23
|
g/cm³
|
ASTM D 792
|
|
Mold Shrinkage, flow, 24 hrs (5)
|
1.5
|
%
|
ASTM D 955
|
|
Mold Shrinkage, xflow, 24 hrs (5)
|
2
|
%
|
ASTM D 955
|
Source GMD, last updated:2004/09/30
|
Processing
pa66 |
Parameter | ||
Injection Molding
|
Value | Unit |
Drying Temperature
|
80
|
°C
|
Drying Time
|
4
|
hrs
|
Maximum Moisture Content
|
0.15 - 0.25
|
%
|
Melt Temperature
|
275 - 290
|
°C
|
Front - Zone 3 Temperature
|
295 - 305
|
°C
|
Middle - Zone 2 Temperature
|
280 - 295
|
°C
|
Rear - Zone 1 Temperature
|
265 - 275
|
°C
|
Mold Temperature
|
80 - 95
|
°C
|
Back Pressure
|
0.2 - 0.3
|
MPa
|
Screw Speed
|
30 - 60
|
rpm
|
Source GMD, last updated:2004/09/30
|