| 三菱丽阳株式会社 PMMA IR-D70 塑胶原料物性数据 |
| 暂无此原料描述部分┄ |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr | ASTM D-570 | 0.4 | % |
| 熔体流动速率 | 230°C.3.8kg | ASTM D-1238 | 1.3 | g/10min | |
| 物理性能 | 折射率 | --- | ASTM D-542 | 1.49 | nd |
| 比重 | --- | ASTM D-792 | 1.14 | --- | |
| 全光线透射系数 | 3.2mm | ASTM D-1003 | 92 | % | |
| 机械性能 | 成形收缩率 | --- | ASTM D-955 | 0.4-0.8 | % |
| 抗拉强度 | ASTM NO.1 | ASTM D-638 | 300 | Kg/cm2 | |
| 延展率 | ASTM NO.1 | ASTM D-638 | 90 | % | |
| 抗弯强度 | 1/4"棒 | ASTM D-790 | 400 | Kg/cm2 | |
| 弯曲弹性模量 | 1/4"棒 | ASTM D-790 | 1.3×104 | Kg/cm2 | |
| 悬臂梁式冲击强度 | 1/4"付 | ASTM D-256 | 7 | kg.cm/cm | |
| 洛氏硬度 | M scale | ASTM D-785 | 32 | --- | |
| 电气性能 | 表面电阻系数 | --- | JIS K-6911 | >1016 | Ω |
| 体积电阻系数 | --- | JIS K-6911 | >1015 | Ω.m | |
| 绝缘击穿强度 | --- | JIS K-6911 | 15 | kv/mm | |
| 介电常数 | 60HZ | JIS K-6911 | 3.9 | --- | |
| 介质损耗角正切 | 60HZ | JIS K-6911 | 0.04 | --- | |
| 耐电弧性 | --- | JIS K-6911 | 没有痕迹 | --- | |
| 热 性 能 | 维卡软化温度 | 1kg | ASTM D-1525 | 95 | °C |
| 比热 | --- | --- | 0.35 | cal/g/°C | |
| 线膨胀系数 | --- | ASTM D-696 | 11.5×10-5 | cm/cm/°C | |
| 热传导系数 | --- | ASTM D-177 | 5×10-4 | cal/s/cm/°C | |
| 载荷挠曲温度 | 18.56kg/cm2 | ASTM D-648 | 80 | °C | |