| 法国阿托菲纳公司 PMMA V045-100 塑胶原料物性数据 |
| 规格级别： | 耐热级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | --- | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 2.3 | g/10min |
| 吸水率 | 浸水24hrs后增重 | ASTM D-570 | 0.3 | % | |
| 物理性能 | 成形收缩率 | (冷模/冷件),48hrs | ASTM D-935 | 0.2-0.6 | % |
| 透光率 | --- | ASTM D-1003 | 92 | % | |
| 折射率ND | --- | ASTM D-542 | 1.49 | --- | |
| 比重 | --- | ASTM D-792 | 1.19 | --- | |
| 雾度 | --- | --- | <2 | % | |
| 机械性能 | 洛氏硬度 | --- | ASTM D-758 | 96 | M scale |
| 拉伸强度 | 初级应变速率0.1cm/cm/min | ASTM D-638 | 720(70) | kgf/cm2 | |
| 弯曲强度 | 横跨比=16 | ASTM D-790 | 1050(103) | kgf/cm2(MPa) | |
| 弯曲模数 | --- | ASTM D-790 | 32000 | kgf/cm2 | |
| 冲击强度 | Izod研磨缺口 | ASTM D-256 | 1.2(12.3) | kgf.cm/cm(J/m) | |
| 冲击强度 | 落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm) | ASTM D-256 | 14(1.4) | kg.cm(J) | |
| 热 性 能 | 热变形温度负荷，退火 | 2℃/min,18.6kgf/cm2 | ASTM D-648 | 93 | ℃ |
| 维卡软化点 | 未退火,50℃/hr,1kg | ASTM D-1525 | 103 | ℃ | |
| 维卡软化点 | 未退火,50℃/hr,5kg | ASTM D-1525 | 97 | ℃ | |
| 玻璃化转变温度Tg | --- | --- | 104 | ℃ | |
| 使用温度范围 | 与残余应力大小有关 | --- | 74-88 | ℃ | |