PEI EX99689C 物性表
添加时间:2012-12-28 22:59LNP STAT-KON* HIGH TEMPERATURE RESINS COMPOUND
BALANCE HIGH TEMPERATURE AND ELECTRICAL PROPERTIES
High temperature LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic through conductive, to electromagnetic interference (EMI) shielding.
LNP™ STAT-KON™ Compound PEI EX99689C 塑料数据物性表
Also known as:LNP™ Stat-kon™ Compound PDX-E-99689 CCS
Product reorder name:EX99689C
LNP STAT-KON* EX99689C is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Clean Compounding System.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,break | 1640 | kgf/cm² | ASTM D 638 |
Tensile Strain,break | 1.6 | % | ASTM D 638 |
Tensile Modulus,50mm/min | 118800 | kgf/cm² | ASTM D 638 |
Flexural Stress | 2460 | kgf/cm² | ASTM D 790 |
Flexural Modulus | 110100 | kgf/cm² | ASTM D 790 |
Tensile Stress,break | 137 | MPa | ISO 527 |
Tensile Strain,break | 1.2 | % | ISO 527 |
Tensile Modulus,1mm/min | 12630 | MPa | ISO 527 |
Flexural Stress | 216 | MPa | ISO 178 |
Flexural Modulus | 10310 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 45 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Energy @ peak,23℃ | 116 | cm-kgf | ASTM D 3763 |
Multiaxial Impact | 24 | cm-kgf | ISO 6603 |
Izod Impact,unnotched 80*10*4 +23℃ | 28 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
HDT,1.82 MPa,3.2mm,unannealed | 205 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 3.33E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 3.29E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 3.33E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 3.30E-05 | 1/℃ | ISO 11359-2 |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 207 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Density | 1.31 | g/cm³ | ASTM D 792 |
Moisture Absorption,50% RH,24 hrs | 0.3 | % | ASTM D 570 |
Mold Shrinkage,flow,24 hrs(5) | 0.2 | % | ASTM D 955 |
Mold Shrinkage,xflow,24 hrs(5) | 0.4 | % | ASTM D 955 |
Mold Shrinkage,flow,24 hrs(5) | 0.17 | % | ISO 294 |
Mold Shrinkage,xflow,24 hrs(5) | 0.36 | % | ISO 294 |
Moisture Absorption(23℃/50% RH) | 0.35 | % | ISO 62 |
ELECTRICAL | Value | Unit | Standard |
Surface Resistivity | 1.E+02-1.E+06 | Ohm | ASTM D 257 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Compliant,94V-0 Flame Class Rating(3)(4) | 0.35 | mm | UL 94 by SABIC-IP |
Source GMD,last updated:2004/10/01 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 120-150 | ℃ |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.05 | % |
Melt Temperature | 360-365 | ℃ |
Front-Zone 3 Temperature | 365-375 | ℃ |
Middle-Zone 2 Temperature | 355-365 | ℃ |
Rear-Zone 1 Temperature | 345-355 | ℃ |
Mold Temperature | 120-150 | ℃ |
Back Pressure | 0.3-0.7 | MPa |
Screw Speed | 60-100 | rpm |
Source GMD,last updated:2004/10/01 |