PEI EX99550C 物性表

添加时间:2012-12-28 22:48

LNP STAT-KON* HIGH TEMPERATURE RESINS COMPOUND
BALANCE HIGH TEMPERATURE AND ELECTRICAL PROPERTIES
High temperature LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound PEI EX99550C 塑料数据物性表

Also known as:LNP™ Stat-kon™ Compound PDX-E-99550 CCS
Product reorder name:EX99550C
LNP STAT-KON* EX99550C is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Clean Compounding System.

MECHANICAL Value Unit Standard
Tensile Stress,break 1930 kgf/cm² ASTM D 638
Tensile Strain,break 1.1 % ASTM D 638
Tensile Modulus,50mm/min 210900 kgf/cm² ASTM D 638
Flexural Stress 2710 kgf/cm² ASTM D 790
Flexural Modulus 191300 kgf/cm² ASTM D 790
Tensile Stress,break 149 MPa ISO 527
Tensile Strain,break 0.7 % ISO 527
Tensile Modulus,1mm/min 22940 MPa ISO 527
Flexural Stress 251 MPa ISO 178
Flexural Modulus 18680 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 35 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 5 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 86 cm-kgf ASTM D 3763
Multiaxial Impact 26 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 24 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 201 ASTM D 648
CTE,-40℃ to 40℃,flow 1.80E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 2.19E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 1.80E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 2.19E-05 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 204 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.37 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.21 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.1 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.3 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.15 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.34 % ISO 294
Moisture Absorption(23℃/50% RH) 0.32 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+00-1.E+04 Ohm ASTM D 257
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant,94V-0 Flame Class Rating(3)(4) 0.35 mm UL 94 by SABIC-IP
Source GMD,last updated:2004/10/01
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Maximum Moisture Content 0.05 %
Melt Temperature 360-365
Front-Zone 3 Temperature 365-375
Middle-Zone 2 Temperature 355-365
Rear-Zone 1 Temperature 345-355
Mold Temperature 120-150
Back Pressure 0.3-0.7 MPa
Screw Speed 60-100 rpm
Source GMD,last updated:2004/10/01