湘樟:PEEK - PTFE - PPE - PVDF - SBS - TPV - TPX - PA6 - PBE - SBR - PVC - PSU - SAN - PA66 - HIPS - 聚四氟乙烯
| PC G-2510 日本出光石油化学株式会社 pc塑料价格物性数据 |
| 规格级别： | 一般级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 特性：增强10% | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||||||
| 基本性能 | 吸水率 | 23℃水中24h | ASTM D-570 | 0.15 | % | |||||||
| 物理性能 | 比重 | --- | ASTM D-792 | 1.27 | --- | |||||||
| 螺线流动长度 | 3mm厚 | 出光法 | 32 | cm | ||||||||
| 机械性能 | 引张降伏强度 | --- | ISO R-527 (ASTM D-638) | 88(900) | MPa(KG/cm2) | |||||||
| 引张破坏强度 | --- | ISO R-527 (ASTM D-638) | 83(850) | MPa(KG/cm2) | ||||||||
| 引张弹性率 | --- | ISO R-527 (ASTM D-638) | 3920(40000) | MPa(KG/cm2) | ||||||||
| 引张破坏伸率 | --- | ISO R-527 (ASTM D-638) | 5 | % | ||||||||
| 挠曲强度 | --- | ISO 178 (ASTM D-790) | 120(1200) | MPa | ||||||||
| 挠曲弹性率 | --- | ISO 178 (ASTM D-790) | 3920(40000) | MPa(KG/cm2) | ||||||||
| IZOD冲击强度 | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 10(10) | KJ/m2(kgfcm/cm2) | ||||||||
| 洛氏硬度 | --- | ISO 2039-2 (ASTM D-785) | M90 | --- | ||||||||
| 电气性能 | 绝缘破坏电压 | 1.6mm厚 | ASTM D-149 | ＜22 | kv/mm | |||||||
| 体积固有抵抗 | --- | ASTM D-257 | ＜1010 | Ω・cm | ||||||||
| 诱电率 | 60Hz | ASTM D-150 | 3.10 | --- | ||||||||
| 诱电率 | 106Hz | ASTM D-150 | 2.95 | --- | ||||||||
| 诱电正接 | 60Hz | ASTM D-150 | 8×10-4 | --- | ||||||||
| 诱电正接 | 106Hz | ASTM D-150 | 9×10-3 | --- | ||||||||
| 耐电弧性 | --- | ASTM D-495 | 110 | Sec | ||||||||
| 加工性能 |
|
--- |
|
|
--- | |||||||
| 热 性 能 | 燃烧性 | 1.47mm厚 | UL 94 | V-2 | --- | |||||||
| 维卡软化点 | --- | ISO 306 | 150 | ℃ | ||||||||
| 线膨胀系数 | --- | ASTM D-696 | 4.5 | ×10-5cm/cm/℃ | ||||||||
| 负荷挠曲温度 | 1.80MPa,18.6kg/cm2 | ISO 75(ASTM D-648) | 136 | ℃ | ||||||||