PBT 1001G10 南通开普乐工程塑料有限公司 物性数据 |
规格级别: | 增强级 | 外观颜色: | --- |
用途概述: | --- | ||
备注说明: | 特性:10%玻纤普通增强,未阻燃。 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||||
物理性能 | 密度 | --- | ASTM D-792 | 1.4 | g/cm3 | ||||||||||
吸水率 | 23℃/24hr | ASTM D-570 | 0.08 | % | |||||||||||
成型收缩率 | --- | ASTM D-955 | 0.6-1.0 | % | |||||||||||
机械性能 | 拉伸强度 | --- | ASTM D-792 | 92 | MPa | ||||||||||
断裂伸长率 | --- | ASTM D-638 | 4 | % | |||||||||||
弯曲强度 | --- | ASTM D-790 | 160 | MPa | |||||||||||
弯曲模量 | --- | ASTM D-790 | 5*103 | MPa | |||||||||||
|
|
|
|
|
|||||||||||
电气性能 | 介电常数 | --- | ASTM D-150 | 3.3 | --- | ||||||||||
介质损耗角正切 | --- | ASTM D-150 | 0.02 | --- | |||||||||||
体积电阻率 | --- | ASTM D-257 | 1.2*1016 | Ω.m | |||||||||||
介电强度 | 2mm厚 | ASTM D-149 | 21 | MV/M | |||||||||||
热 性 能 | 热变形温度 | 1.82MPa | ASTM D-648 | 192 | ℃ | ||||||||||
燃烧性 | --- | UL 94 | HB | --- |
PBT 1001G20 南通开普乐工程塑料有限公司 物性数据 |
规格级别: | 增强级 | 外观颜色: | --- |
用途概述: | --- | ||
备注说明: | 特性:20%玻纤普通增强,未阻燃 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||||
物理性能 | 密度 | --- | ASTM D-792 | 1.44 | g/cm3 | ||||||||||
吸水率 | 23℃/24hr | ASTM D-570 | 0.08 | % | |||||||||||
成型收缩率 | --- | ASTM D-955 | 0.3-0.8 | % | |||||||||||
机械性能 | 拉伸强度 | --- | ASTM D-792 | 114 | MPa | ||||||||||
断裂伸长率 | --- | ASTM D-638 | 4 | % | |||||||||||
弯曲强度 | --- | ASTM D-790 | 178 | MPa | |||||||||||
弯曲模量 | --- | ASTM D-790 | 6.5*103 | MPa | |||||||||||
|
|
|
|
|
|||||||||||
电气性能 | 介电常数 | --- | ASTM D-150 | 3.3 | --- | ||||||||||
介质损耗角正切 | --- | ASTM D-150 | 0.02 | --- | |||||||||||
体积电阻率 | --- | ASTM D-257 | 1.2*1016 | Ω.m | |||||||||||
介电强度 | 2mm厚 | ASTM D-149 | 21 | MV/M | |||||||||||
热 性 能 | 热变形温度 | 1.82MPa | ASTM D-648 | 200 | ℃ | ||||||||||
燃烧性 | --- | UL 94 | HB | --- |
PBT 1001G30 南通开普乐工程塑料有限公司 物性数据 |
规格级别: | 增强级 | 外观颜色: | --- |
用途概述: | --- | ||
备注说明: | 特性:30%玻纤普通增强,未阻燃。 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||||
物理性能 | 密度 | --- | ASTM D-792 | 1.55 | g/cm3 | ||||||||||
吸水率 | 23℃/24hr | ASTM D-570 | 0.08 | % | |||||||||||
成型收缩率 | --- | ASTM D-955 | 0.2-0.7 | % | |||||||||||
机械性能 | 拉伸强度 | --- | ASTM D-792 | 122 | MPa | ||||||||||
断裂伸长率 | --- | ASTM D-638 | 4 | % | |||||||||||
弯曲强度 | --- | ASTM D-790 | 190 | MPa | |||||||||||
弯曲模量 | --- | ASTM D-790 | 8.4*103 | MPa | |||||||||||
|
|
|
|
|
|||||||||||
电气性能 | 介电常数 | --- | ASTM D-150 | 3.3 | --- | ||||||||||
介质损耗角正切 | --- | ASTM D-150 | 0.02 | --- | |||||||||||
体积电阻率 | --- | ASTM D-257 | 1.2*1016 | Ω.m | |||||||||||
介电强度 | 2mm厚 | ASTM D-149 | 21 | MV/M | |||||||||||
热 性 能 | 热变形温度 | 1.82MPa | ASTM D-648 | 205 | ℃ | ||||||||||
燃烧性 | --- | UL 94 | HB | --- |