湘樟:PEEK - PTFE - PPE - PVDF - SBS - TPV - TPX - PA6 - PBE - SBR - PVC - PSU - SAN - PA66 - HIPS - 聚四氟乙烯
| ABS TE-10 日本电气化学工业株式会社 物性数据 |
| 规格级别： | --- | 外观颜色： | 透明 |
| 用途概述： | --- | ||
| 备注说明： | 特点：标准 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃×5N | ASTM D-1238 | 2.2 | g/10min |
| 熔体流动速率 | 220℃×100N | ASTM D-1238 | 30 | g/10min | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.09 | --- |
| 全光线透过率 | 2mm | ASTM D-1003 | 90 | % | |
| 雾度 | 2mm | ASTM D-1003 | 1.8 | % | |
| 成型收缩率 | 2mm | --- | 0.4-0.6 | % | |
| 燃烧性 | --- | UL 94 | 1.5mmHB | --- | |
| 机械性能 | 洛氏硬度 | --- | ASTM D-785 | 111 | R |
| 洛氏硬度 | --- | ASTM D-785 | 50 | M | |
| 弯曲弹性模量 | --- | ASTM D-790 | 2100 | MPa | |
| 拉伸强度 | --- | ASTM D-638 | 40 | MPa | |
| 弯曲强度 | --- | ASTM D-790 | 68 | MPa | |
| IZOD冲击强度 | 1/4〃带缺口 | ASTM D-256 | 155 | J/m | |
| 热 性 能 | 热变形温度 | 12.7mm,1.82MPa | ASTM D-648 | 87 | ℃ |
| 维卡软化点 | 50N | ASTM D-1525 | 90 | ℃ | |
| 热变形温度 | 6.4mm,1.82MPa | ASTM D-648 | 83 | ℃ | |
| ABS TE-20 日本电气化学工业株式会社 abs塑料物性数据 |
| 规格级别： | --- | 外观颜色： | 透明 |
| 用途概述： | --- | ||
| 备注说明： | 特性：耐热高刚性 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃×5N | ASTM D-1238 | 2.3 | g/10min |
| 熔体流动速率 | 220℃×100N | ASTM D-1238 | 32 | g/10min | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.10 | --- |
| 全光线透过率 | 2mm | ASTM D-1003 | 90 | % | |
| 雾度 | 2mm | ASTM D-1003 | 1.5 | % | |
| 成型收缩率 | 2mm | --- | 0.4-0.6 | % | |
| 机械性能 | 洛氏硬度 | --- | ASTM D-785 | 115 | R |
| 洛氏硬度 | --- | ASTM D-785 | 58 | M | |
| 弯曲弹性模量 | --- | ASTM D-790 | 2400 | MPa | |
| 拉伸强度 | --- | ASTM D-638 | 44 | MPa | |
| 弯曲强度 | --- | ASTM D-790 | 76 | MPa | |
| IZOD冲击强度 | 1/4〃带缺口 | ASTM D-256 | 110 | J/m | |
| 热 性 能 | 热变形温度 | 12.7mm,1.82MPa | ASTM D-648 | 89 | ℃ |
| 维卡软化点 | 50N | ASTM D-1525 | 94 | ℃ | |
| 热变形温度 | 6.4mm,1.82MPa | ASTM D-648 | 86 | ℃ | |
| 燃烧性 | --- | UL 94 | 1.5mmHB | --- | |
| ABS TE-30 日本电气化学工业株式会社 物性数据 |
| 规格级别： | --- | 外观颜色： | 透明 |
| 用途概述： | --- | ||
| 备注说明： | 特性：高抗冲 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃×5N | ASTM D-1238 | 2.0 | g/10min |
| 熔体流动速率 | 220℃×100N | ASTM D-1238 | 28 | g/10min | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.09 | --- |
| 全光线透过率 | 2mm | ASTM D-1003 | 90 | % | |
| 雾度 | 2mm | ASTM D-1003 | 2.0 | % | |
| 成型收缩率 | 2mm | --- | 0.4-0.6 | % | |
| 机械性能 | 洛氏硬度 | --- | ASTM D-785 | 110 | R |
| 洛氏硬度 | --- | ASTM D-785 | 46 | M | |
| 弯曲弹性模量 | --- | ASTM D-790 | 1950 | MPa | |
| 拉伸强度 | --- | ASTM D-638 | 37 | MPa | |
| 弯曲强度 | --- | ASTM D-790 | 62 | MPa | |
| IZOD冲击强度 | 1/4〃带缺口 | ASTM D-256 | 185 | J/m | |
| 热 性 能 | 热变形温度 | 12.7mm,1.82MPa | ASTM D-648 | 84 | ℃ |
| 维卡软化点 | 50N | ASTM D-1525 | 85 | ℃ | |
| 热变形温度 | 6.4mm,1.82MPa | ASTM D-648 | 80 | ℃ | |
| 燃烧性 | --- | UL 94 | 1.5mmHB | --- | |