快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ STAT-KON™ Compound ABS AX02747 塑料物性表
Also known as:LNP™ Stat-kon™ Compound PDX-A-02747 Product reorder name:AX02747
LNP* Stat-kon* AX02747 is a compound based on Acrylonitrile Butadiene Styrene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,brk,Type I,5mm/min | 1450 | kgf/cm² | ASTM D 638 |
Tensile Strain,brk,Type I,5mm/min | 0.9 | % | ASTM D 638 |
Tensile Modulus,50mm/min | 306500 | kgf/cm² | ASTM D 638 |
Flexural Stress,brk,1.3mm/min,50mm span | 2030 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3mm/min,50mm span | 241600 | kgf/cm² | ASTM D 790 |
Tensile Stress,break,5mm/min | 141 | MPa | ISO 527 |
Tensile Strain,break,5mm/min | 0.9 | % | ISO 527 |
Tensile Modulus,1mm/min | 25300 | MPa | ISO 527 |
Flexural Stress | 215 | MPa | ISO 178 |
Flexural Modulus,2mm/min | 24670 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 32 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 6 | cm-kgf/cm | ASTM D 256 |
Multiaxial Impact | 27 | cm-kgf | ISO 6603 |
Instrumented Impact Total Energy,23℃ | 61 | cm-kgf | ASTM D 3763 |
Izod Impact,unnotched 80*10*4 +23℃ | 18 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,3.2mm,unannealed | 106 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 101 | ℃ | ASTM D 648 |
CTE,-30℃ to 30℃,flow | 2.10E-05 | 1/℃ | ASTM D 696 |
CTE,-30℃ to 30℃,xflow | 2.50E-05 | 1/℃ | ASTM D 696 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 107 | ℃ | ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 101 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.27 | - | ASTM D 792 |
Density | 1.27 | g/cm³ | ASTM D 792 |
Moisture Absorption,50% RH,24 hrs | 0.17 | % | ASTM D 570 |
Mold Shrinkage,flow,24 hrs(5) | 0.1-0.3 | % | ASTM D 955 |
Mold Shrinkage,xflow,24 hrs(5) | 0.3-0.5 | % | ASTM D 955 |
Moisture Absorption(23℃/50% RH) | 0.24 | % | ISO 62 |
ELECTRICAL | Value | Unit | Standard |
Surface Resistivity | 2.E+00-6.E+00 | Ohm | ASTM D 257 |
Source GMD,last updated:2010/10/27 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80 | ℃ |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.05-0.1 | % |
Melt Temperature | 260 | ℃ |
Front-Zone 3 Temperature | 265-275 | ℃ |
Middle-Zone 2 Temperature | 230-245 | ℃ |
Rear-Zone 1 Temperature | 205-215 | ℃ |
Mold Temperature | 70-80 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |