ABS AX00756 含不锈钢的化合物,导电ABS
  • 产 品:ABS AX00756 含不锈钢的化合物,导电ABS
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP STAT-KON* POLYCARBONATE COMPOUND
STRENGTH PLUS TAILORED ELECTRICAL PROPERTIES
Polycarbonate-based LNP Stat-Kon compounds contain electrically active additives that provide controlled surface resistivity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding.

LNP™ STAT-KON™ Compound ABS AX00756 塑料物性表

Also known as:LNP™ Stat-kon™ Compound PDX-A-00756 EXP
Product reorder name:AX00756
LNP STAT-KON* AX00756 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive.

MECHANICAL Value Unit Standard
Tensile Stress,yield 300 kgf/cm² ASTM D 638
Tensile Stress,break 300 kgf/cm² ASTM D 638
Tensile Strain,yield 1.8 % ASTM D 638
Tensile Strain,break 1.8 % ASTM D 638
Tensile Modulus,50mm/min 30200 kgf/cm² ASTM D 638
Flexural Stress 620 kgf/cm² ASTM D 790
Flexural Modulus 29000 kgf/cm² ASTM D 790
Tensile Stress,yield 30 MPa ISO 527
Tensile Stress,break 28 MPa ISO 527
Tensile Strain,yield 1.7 % ISO 527
Tensile Strain,break 5.4 % ISO 527
Tensile Modulus,1mm/min 2580 MPa ISO 527
Flexural Stress 58 MPa ISO 178
Flexural Modulus 2570 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 21 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 84 cm-kgf ASTM D 3763
Multiaxial Impact 5 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 14 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 91 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 80 ASTM D 648
CTE,-40℃ to 40℃,flow 6.98E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 7.55E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 6.98E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 7.56E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 93 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 82 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.165 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.35 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.7 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.8 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.7 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.78 % ISO 294
Density 1.16 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.3 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+01-1.E+05 Ohm ASTM D 257
Source GMD,last updated:2004/10/01
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.05-0.1 %
Melt Temperature 260
Front-Zone 3 Temperature 265-275
Middle-Zone 2 Temperature 230-245
Rear-Zone 1 Temperature 205-215
Mold Temperature 70-80
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/10/01

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.