LNP* Colorcomp* Compound
LNP Colorcomp All Series
LNP* Colorcomp* resins contain colorants and special effects for a dazzling spectrum of colored materials. Among the offerings are opaque, translucent, and transparent resins, plus special effects, including edge glow, sparkle, glow, pearlescent, and thermochromic. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™Colorcomp™ Compound ABS AX98567H 数据
LNP* Colorcomp* AX98567H is a compound based on ABS containing Proprietary Fillers. Characteristics of this grade are: Healthcare.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yield,5mm/min | 52 | MPa | ISO 527 |
Tensile Strain,yield,5mm/min | 2 | % | ISO 527 |
Tensile Strain,break,5mm/min | 15 | % | ISO 527 |
Tensile Modulus,1mm/min | 2500 | MPa | ISO 527 |
Flexural Stress | 75 | MPa | ISO 178 |
Flexural Modulus,2mm/min | 2600 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Charpy Impact,unnotched,-30℃ | 70 | kJ/m² | ISO 179/2C |
Izod Impact,notched 80*10*4 +23℃ | 12 | kJ/m² | ISO 180/1A |
Charpy Impact,notched,23℃ | 11 | kJ/m² | ISO 179/2C |
THERMAL | Value | Unit | Standard |
CTE,23℃ to 60℃,flow | 8.00E-05 | 1/℃ | ISO 11359-2 |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.06 | - | ASTM D 792 |
Mold Shrinkage,flow,24 hrs(5) | 0.4-0.6 | % | ISO 294 |
Mold Shrinkage,xflow,24 hrs(5) | 0.4-0.6 | % | ISO 294 |
Melt Volume Rate,MVR at 220℃/10.0 kg | 16 | cm³/10 min | ISO 1133 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 1.00E+16 | Ohm-cm | IEC 60093 |
Surface Resistivity,ROA | 1.00E+16 | Ohm | IEC 60093 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized,94HB Flame Class Rating(3) | 1.6 | mm | UL 94 |
Source GMD,last updated:2011/06/20 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80 | ℃ |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.05-0.1 | % |
Melt Temperature | 260 | ℃ |
Front-Zone 3 Temperature | 265-275 | ℃ |
Middle-Zone 2 Temperature | 230-245 | ℃ |
Rear-Zone 1 Temperature | 205-215 | ℃ |
Mold Temperature | 70-80 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2011/06/20 |
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.ABS PA-797 耐HCFC
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字:【LNP™Colorcomp™ Compound ABS AX98567H】