Geloy* Resin
Geloy Weatherable
Geloy* advanced amorphous terpolymer of acrylic-styrene-acrylonitrile (ASA) resins are among the most weatherable grades in SABIC Innovative Plastics' portfolio. In addition to exterior stability, advanced grades of Geloy resin and blends offer great aesthetics, color options, good chemical resistance, high heat performance, and processability.
Geloy* Resin ASA XP7550 数据
Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow.
Property
TYPICAL PROPERTIES (1)
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50 mm/min | 570 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,50 mm/min | 440 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,50 mm/min | 4 | % | ASTM D 638 |
Tensile Strain,brk,Type I,50 mm/min | 40 | % | ASTM D 638 |
Tensile Modulus,5 mm/min | 26000 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span | 830 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 25200 | kgf/cm² | ASTM D 790 |
Hardness,Rockwell R | 109 | - | ASTM D 785 |
Tensile Stress,yield,50 mm/min | 55 | MPa | ISO 527 |
Tensile Stress,break,50 mm/min | 44 | MPa | ISO 527 |
Tensile Strain,yield,50 mm/min | 3.8 | % | ISO 527 |
Tensile Strain,break,50 mm/min | 37 | % | ISO 527 |
Tensile Modulus,1 mm/min | 2550 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 74 | MPa | ISO 178 |
Flexural Modulus,2 mm/min | 2400 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 38 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,-30℃ | 5 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Total Energy,23℃ | 367 | cm-kgf | ASTM D 3763 |
Instrumented Impact Total Energy,-30℃ | 101 | cm-kgf | ASTM D 3763 |
Izod Impact,notched 80*10*4 +23℃ | 35 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 9 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp,Rate B/50 | 105 | ℃ | ASTM D 1525 |
HDT,0.45 MPa,3.2 mm,unannealed | 104 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 89 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 7.20E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 7.90E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 7.20E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 7.80E-05 | 1/℃ | ISO 11359-2 |
Ball Pressure Test,75℃ +/- 2℃ | 85 | - | IEC 60695-10-2 |
Vicat Softening Temp,Rate B/50 | 105 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 106 | ℃ | ISO 306 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 103 | ℃ | ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 89 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.11 | - | ASTM D 792 |
Mold Shrinkage on Tensile Bar,flow (2) (5) | 0.5-0.7 | % | SABIC Method |
Mold Shrinkage,flow,3.2 mm (5) | 0.4-0.6 | % | SABIC Method |
Mold Shrinkage,xflow,3.2 mm (5) | 0.5-0.7 | % | SABIC Method |
Melt Flow Rate,220℃/10.0 kgf | 14 | g/10 min | ASTM D 1238 |
Density | 1.11 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.8 | % | ISO 62 |
Moisture Absorption (23℃ / 50% RH) | 0.3 | % | ISO 62 |
Melt Volume Rate,MVR at 260℃/5.0 kg | 26 | cm³/10 min | ISO 1133 |
OPTICAL | Value | Unit | Standard |
Gloss,untextured,60 degrees | 94 | - | ASTM D 523 |
Source GMD,last updated:2004/04/29 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 90-100 | ℃ |
Drying Time | 3-4 | hrs |
Drying Time (Cumulative) | 8 | hrs |
Maximum Moisture Content | 0.04 | % |
Melt Temperature | 255-270 | ℃ |
Nozzle Temperature | 240-255 | ℃ |
Front-Zone 3 Temperature | 245-260 | ℃ |
Middle-Zone 2 Temperature | 240-255 | ℃ |
Rear-Zone 1 Temperature | 230-250 | ℃ |
Mold Temperature | 55-70 | ℃ |
Back Pressure | 0.3-1 | MPa |
Screw Speed | 30-80 | rpm |
Shot to Cylinder Size | 40-80 | % |
Vent Depth | 0.038-0.076 | mm |
Source GMD,last updated:2004/04/29 |
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健词:ASA XP7550 沙伯基础创新ASA塑料代理:http://www.pa66-suliao.com/product/tysuliao/SAN/