联系我们
- 产 品：ASA XP4025 ASA加PC,耐候级
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Geloy* Resin
Geloy Weatherable
Geloy* advanced amorphous terpolymer of acrylic-styrene-acrylonitrile (ASA) resins are among the most weatherable grades in SABIC Innovative Plastics' portfolio. In addition to exterior stability, advanced grades of Geloy resin and blends offer great aesthetics, color options, good chemical resistance, high heat performance, and processability.
Geloy* Resin XP4025 数据
Available in a wide range of colors and is recommended for unpainted exterior applications.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50 mm/min | 600 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,50 mm/min | 25 | % | ASTM D 638 |
| Flexural Stress,yld,1.3 mm/min,50 mm span | 890 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3 mm/min,50 mm span | 26300 | kgf/cm² | ASTM D 790 |
| Hardness,Rockwell R | 114 | - | ASTM D 785 |
| Tensile Stress,yield,50 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress,break,50 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain,yield,50 mm/min | 4.1 | % | ISO 527 |
| Tensile Strain,break,50 mm/min | 64 | % | ISO 527 |
| Tensile Modulus,1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress,yield,2 mm/min | 75 | MPa | ISO 178 |
| Flexural Modulus,2 mm/min | 2500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 17 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 6 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 397 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-30℃ | 345 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 21 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 5 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 37 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2 mm,unannealed | 102 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,6.4 mm,unannealed | 90 | ℃ | ASTM D 648 |
| CTE,-20℃ to 150℃,flow | 7.20E-05 | 1/℃ | ASTM E 831 |
| CTE,-20℃ to 150℃,xflow | 7.20E-05 | 1/℃ | ASTM E 831 |
| Thermal Conductivity | 0.25 | W/m-℃ | ASTM C 177 |
| Vicat Softening Temp,Rate B/50 | 109 | ℃ | ISO 306 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 107 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 93 | ℃ | ISO 75/Af |
| Relative Temp Index,Elec | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 50 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.14 | - | ASTM D 792 |
| Water Absorption,24 hours | 0.24 | % | ASTM D 570 |
| Mold Shrinkage,flow,3.2 mm (5) | 0.5-0.7 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2 mm (5) | 0.5-0.7 | % | SABIC Method |
| Melt Flow Rate,220℃/10.0 kgf | 6.7 | g/10 min | ASTM D 1238 |
| Melt Flow Rate,260℃/5.0 kgf | 18 | g/10 min | ASTM D 1238 |
| Melt Flow Rate,280℃/3.8 kgf | 31 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Gloss,untextured,60 degrees | 90 | - | ASTM D 523 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Source GMD,last updated:2000/01/05 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 90-100 | ℃ |
| Drying Time | 3-4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 255-270 | ℃ |
| Nozzle Temperature | 240-255 | ℃ |
| Front-Zone 3 Temperature | 245-260 | ℃ |
| Middle-Zone 2 Temperature | 240-255 | ℃ |
| Rear-Zone 1 Temperature | 230-250 | ℃ |
| Mold Temperature | 55-70 | ℃ |
| Back Pressure | 0.3-1 | MPa |
| Screw Speed | 30-80 | rpm |
| Shot to Cylinder Size | 40-80 | % |
| Vent Depth | 0.038-0.076 | mm |
| Parameter Sheet Extrusion | Value | Unit |
| Drying Temperature | 90-100 | ℃ |
| Drying Time | 3-4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Minimum Moisture Content | 0.04 | % |
| Melt Temperature | 255-270 | ℃ |
| Barrel-Zone 1 Temperature | 220-230 | ℃ |
| Barrel-Zone 2 Temperature | 230-245 | ℃ |
| Barrel-Zone 3 Temperature | 245-255 | ℃ |
| Barrel-Zone 4 Temperature | 255-265 | ℃ |
| Adapter Temperature | 255-265 | ℃ |
| Die Temperature | 255-265 | ℃ |
| Roll Stack Temp-Top | 100-120 | ℃ |
| Roll Stack Temp-Middle | 95-110 | ℃ |
| Roll Stack Temp-Bottom | 75-90 | ℃ |
| Source GMD,last updated:2000/01/05 | ||
• May be used in co-extrusion or monolayer.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
沙伯基础创新ASA塑料代理：http://www.pa66-suliao.com/product/tysuliao/SAN/