- 产 品：ASA CR3020 低光泽
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Geloy* Resin
Geloy Weatherable
Geloy* advanced amorphous terpolymer of acrylic-styrene-acrylonitrile (ASA) resins are among the most weatherable grades in SABIC Innovative Plastics' portfolio. In addition to exterior stability, advanced
grades of Geloy resin and blends offer great aesthetics, color options, good chemical resistance, high heat performance, and processability.
Geloy* Resin ASA CR3020 数据
Low-gloss ASA for profile and capstock applications
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50 mm/min | 390 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50 mm/min | 300 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50 mm/min | 3.5 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50 mm/min | 38 | % | ASTM D 638 |
| Tensile Modulus,5 mm/min | 18700 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3 mm/min,50 mm span | 580 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3 mm/min,50 mm span | 18900 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,50 mm/min | 39 | MPa | ISO 527 |
| Tensile Stress,break,50 mm/min | 31 | MPa | ISO 527 |
| Tensile Strain,yield,50 mm/min | 3.4 | % | ISO 527 |
| Tensile Strain,break,50 mm/min | 23 | % | ISO 527 |
| Tensile Modulus,1 mm/min | 1800 | MPa | ISO 527 |
| Flexural Stress,yield,2 mm/min | 56 | MPa | ISO 178 |
| Flexural Modulus,2 mm/min | 1800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 0 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 0 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 45 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 25 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 3 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 100 | ℃ | ASTM D 1525 |
| HDT,1.82 MPa,3.2mm,unannealed | 74 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 1.40E-04 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 2.00E-04 | 1/℃ | ISO 11359-2 |
| Vicat Softening Temp,Rate B/50 | 100 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 77 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.07 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2 mm (5) | 0.55-0.63 | % | SABIC Method |
| Melt Flow Rate,220℃/10.0 kgf | 5 | g/10 min | ASTM D 1238 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Flow Rate,220℃/10.0 kg | 6 | g/10 min | ISO 1133 |
| Source GMD,last updated:2009/08/27 | |||
| Parameter Profile Extrusion | Value | Unit |
| Drying Temperature | 80-90 | ℃ |
| Drying Time | 3-6 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature | 225-255 | ℃ |
| Barrel-Zone 1 Temperature | 205-215 | ℃ |
| Barrel-Zone 2 Temperature | 215-230 | ℃ |
| Barrel-Zone 3 Temperature | 220-240 | ℃ |
| Barrel-Zone 4 Temperature | 225-245 | ℃ |
| Adapter Temperature | 225-245 | ℃ |
| Die Temperature | 225-245 | ℃ |
| Calibrator Temperature | 15-65 | ℃ |
| Source GMD,last updated:2009/08/27 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.