- 产 品：PP MX10301C 含专有填料,是一个静态导电聚丙烯
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ STAT-KON™ Compound PP MX10301C 塑料物性表
Also known as:LNP™Stat-kon™Compound MX10301C Product reorder name:MX10301C
LNP* Stat-Kon* MX10301C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 320 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 200 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 7.5 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 25.5 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 18000 | kgf/cm² | ASTM D 638 |
| Flexural Modulus,1.3mm/min,50mm span | 15100 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 31 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 22 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 6.6 | % | ISO 527 |
| Tensile Strain,break,5mm/min | 18 | % | ISO 527 |
| Tensile Modulus,1mm/min | 1570 | MPa | ISO 527 |
| Flexural Stress | 35 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 1510 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 149 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 13 | cm-kgf/cm | ASTM D 256 |
| Multiaxial Impact | 326 | cm-kgf | ISO 6603 |
| Instrumented Impact Total Energy,23℃ | 377 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | 141 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 95 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 53 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 9.20E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 9.50E-05 | 1/℃ | ASTM E 831 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 89 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 52 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 0.98 | - | ASTM D 792 |
| Density | 0.98 | g/cm³ | ASTM D 792 |
| Moisture Absorption,50% RH,24 hrs | 0.02 | % | ASTM D 570 |
| Mold Shrinkage,flow(5) | 1 | % | SABIC Method |
| Mold Shrinkage,xflow(5) | 2 | % | SABIC Method |
| Moisture Absorption(23℃/50% RH) | 0.01 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 3.00E+00 | Ohm | ASTM D 257 |
| Source GMD,last updated:2011/06/20 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 225-250 | ℃ |
| Front-Zone 3 Temperature | 240-250 | ℃ |
| Middle-Zone 2 Temperature | 215-225 | ℃ |
| Rear-Zone 1 Temperature | 195-205 | ℃ |
| Mold Temperature | 30-50 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD, last updated:2011/06/20 | ||