PU TX97446 含专有填料的聚氨酯化合物,内部润滑
  • 产 品:PU TX97446 含专有填料的聚氨酯化合物,内部润滑
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

NP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ LUBRICOMP™ Compound PU TX97446 塑料数据

Also known as:LNP™ Lubricomp™ Compound PDX-T-97446 BK8-115
Product reorder name:TX97446
LNP* Lubricomp* TX97446 is a compound based on Polyurethane containing Proprietary Fillers. Characteristics are: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 230 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 54 % ASTM D 638
Tensile Modulus,5mm/min 5700 kgf/cm² ASTM D 638
Flexural Modulus,1.3mm/min,50mm span 3500 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 23 MPa ISO 527
Tensile Strain,yield,5mm/min 51 % ISO 527
Tensile Modulus,1mm/min 410 MPa ISO 527
Flexural Stress 13 MPa ISO 178
Flexural Modulus,2mm/min 380 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 123 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 23 cm-kgf/cm ASTM D 256
Multiaxial Impact 385 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 458 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 95 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 18 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 51 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 42 ASTM D 648
CTE,-30℃ to 30℃,flow 1.24E-04 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 1.43E-04 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 61 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 44 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.21 - ASTM D 792
Density 1.21 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.46 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.7-1 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.8-2 % ASTM D 955
Moisture Absorption(23℃/50% RH) 0.66 % ISO 62
Source GMD,last updated:2009/10/14
Parameter Injection Molding Value Unit
Drying Temperature 95-105
Drying Time 2 hrs
Maximum Moisture Content 0.03 %
Melt Temperature 210
Nozzle Temperature 205-225
Front-Zone 3 Temperature 200-220
Middle-Zone 2 Temperature 195-215
Rear-Zone 1 Temperature 195-210
Mold Temperature 15-45
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Shot to Cylinder Size 40-80 %
Source GMD,last updated:2009/10/14
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.