PES JFL34 含有玻璃纤维和聚四氟乙烯
  • 产 品:PES JFL34 含有玻璃纤维和聚四氟乙烯
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ Lubricomp™ Compound PES JFL34 塑料数据

Also known as:LNP™ Lubricomp™ Compound JFL-4034
Product reorder name:JFL34
LNP* JFL34 is a Polyethersulfone base resin containing glass fiber and PTFE. Characteristics are lubricity.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1060 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 980 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 2.5 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.5 % ASTM D 638
Tensile Modulus,50mm/min 72100 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1490 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3mm/min,50mm span 1480 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 61300 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 103 MPa ISO 527
Tensile Stress,break,5mm/min 94 MPa ISO 527
Tensile Strain,yield,5mm/min 2.5 % ISO 527
Tensile Strain,break,5mm/min 2.5 % ISO 527
Tensile Modulus,1mm/min 7030 MPa ISO 527
Flexural Stress 147 MPa ISO 178
Flexural Modulus,2mm/min 6300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 54 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 7 cm-kgf/cm ASTM D 256
Multiaxial Impact 30 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 143 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 32 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 7 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 219 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 212 ASTM D 648
CTE,-30℃ to 30℃,flow 3.20E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 4.10E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 220 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 212 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.61 - ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.35 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.3-0.5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.5-0.7 % ASTM D 955
Wear Factor Washer 58 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 7 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.46 - ASTM D 3702 Modified
Static COF 0.63 - ASTM D 3702 Modified
Density 1.61 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.52 % ISO 62
Source GMD,last updated:2008/10/16
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Maximum Moisture Content 0.05 %
Melt Temperature 355-370
Front-Zone 3 Temperature 370-380
Middle-Zone 2 Temperature 360-370
Rear-Zone 1 Temperature 345-355
Mold Temperature 140-150
Back Pressure 0.3-0.7 MPa
Screw Speed 60-100 rpm
Source GMD,last updated:2008/10/16

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ Lubricomp™ Compound PES JFL34