PES JX91550 聚醚砜树脂,未填充化合物
  • 产 品:PES JX91550 聚醚砜树脂,未填充化合物
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理
上一篇:没有了 下一篇:PES JX91550 聚醚砜树脂化合物,未填充

LNP Colorcomp* High Temperature Resins Compound
Colors that take the heat
High temperature LNP Colorcomp pre-colored unfilled compounds offer temperature resistance plus a dazzling spectrum of color and effects. Offerings include opaque, translucent, and transparent resins, plus special effects, including edge glow, sparkle, glow, pearlescent, and thermochromic.

LNP™COLORCOMP™ Compound JX91550 数据表

Also known as:LNP™Colorcomp™Compound PDX-J-91550
Product reorder name:JX91550
LNP COLORCOMP* JX91550 is a compound based on Polyethersulfone resin containing Unfilled Custom Color.

MECHANICAL Value Unit Standard
Tensile Stress,yield 780 kgf/cm² ASTM D 638
Tensile Stress,break 590 kgf/cm² ASTM D 638
Tensile Strain,yield 5.6 % ASTM D 638
Tensile Strain,break 13.5 % ASTM D 638
Tensile Modulus,50mm/min 29900 kgf/cm² ASTM D 638
Flexural Stress 1250 kgf/cm² ASTM D 790
Flexural Modulus 29500 kgf/cm² ASTM D 790
Tensile Stress,yield 78 MPa ISO 527
Tensile Stress,break 53 MPa ISO 527
Tensile Strain,yield 6.2 % ISO 527
Tensile Strain,break 23.4 % ISO 527
Tensile Modulus,1mm/min 2830 MPa ISO 527
Flexural Stress 118 MPa ISO 178
Flexural Modulus 2920 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ NB cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 5 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 195 cm-kgf ASTM D 3763
Multiaxial Impact 330 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ NB kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 176 ASTM D 648
CTE,-40℃ to 40℃,flow 5.05E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 5.14E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 5.07E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 5.15E-05 1/℃ ISO 11359-2
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 187 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.49 g/cm³ ASTM D 792
Mold Shrinkage,flow,24 hrs(5) 0.6-0.8 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.7-0.9 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.6-0.8 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.7-0.9 % ISO 294
Density 1.49 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.76 % ISO 62
Source GMD,last updated:2004/10/05
Parameter Injection Molding Value Unit
Drying Temperature 120-150
Drying Time 4 hrs
Maximum Moisture Content 0.05 %
Melt Temperature 355-370
Front-Zone 3 Temperature 370-380
Middle-Zone 2 Temperature 360-370
Rear-Zone 1 Temperature 345-355
Mold Temperature 140-150
Back Pressure 0.3-0.7 MPa
Screw Speed 60-100 rpm
Source GMD,last updated:2004/10/05

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.PBT IQNH2900 无卤阻燃,PBT+PC合金,抗冲击改性
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™Colorcomp™ Compound PES JX91550