LNP™ STAT-KON™ Compound PPS OE006 塑料物性表
LNP* Stat-Kon* OE006 is a compound based on PPS - Linear resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,break | 1890 | kgf/cm² | ASTM D 638 |
Tensile Strain,break | 1.2 | % | ASTM D 638 |
Tensile Modulus,50 mm/min | 243900 | kgf/cm² | ASTM D 638 |
Flexural Stress | 2880 | kgf/cm² | ASTM D 790 |
Flexural Modulus | 215800 | kgf/cm² | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 65 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 7 | cm-kgf/cm | ASTM D 256 |
THERMAL | Value | Unit | Standard |
HDT,1.82 MPa,3.2mm,unannealed | 108 | ℃ | ASTM D 648 |
PHYSICAL | Value | Unit | Standard |
Density | 1.43 | g/cm³ | ASTM D 792 |
Source GMD,last updated:2010/03/16 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 120-150 | ℃ |
Drying Time | 4 | hrs |
Melt Temperature | 315-320 | ℃ |
Front-Zone 3 Temperature | 330-345 | ℃ |
Middle-Zone 2 Temperature | 320-330 | ℃ |
Rear-Zone 1 Temperature | 305-315 | ℃ |
Mold Temperature | 140-165 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2010/03/16 |