- 产 品：PPO PX1390 易于加工,高热量,汽车应用为主
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Noryl* Unreinforced, Multi-purpose Resin
Well-Balanced, Dimensionally Stable
General purpose, unreinforced modified amorphous blends of PPO* resin (polyphenylene ether) and polystyrene.
Noryl* Resin PPO PX1390 数据表
Automotive applications, primarily. Excellent electrical properties, easy processability, high heat, 295F (146C) DTUL.
Property
TYPICAL PROPERTIES(1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 630 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 30 | % | ASTM D 638 |
| Flexural Stress,yld,2.6mm/min,100mm span | 1010 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,2.6mm/min,100mm span | 23200 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 29 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-40℃ | 16 | cm-kgf/cm | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,6.4mm,unannealed | 154 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,6.4mm,unannealed | 146 | ℃ | ASTM D 648 |
| CTE,0℃ to 100℃,flow | 7.20E-05 | 1/℃ | ASTM E 831 |
| Relative Temp Index,Elec | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 50 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 50 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.06 | - | ASTM D 792 |
| Water Absorption,24 hours | 0.1 | % | ASTM D 570 |
| Mold Shrinkage,flow,3.2mm (5) | 0.5-0.7 | % | SABIC Method |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94HB Flame Class Rating (3) | 0.71 | mm | UL 94 |
| Source GMD,last updated:2000/01/05 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 105-110 | ℃ |
| Drying Time | 3-4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 295-315 | ℃ |
| Nozzle Temperature | 295-315 | ℃ |
| Front-Zone 3 Temperature | 280-315 | ℃ |
| Middle-Zone 2 Temperature | 270-310 | ℃ |
| Rear-Zone 1 Temperature | 260-305 | ℃ |
| Mold Temperature | 75-105 | ℃ |
| Back Pressure | 0.3-0.7 | MPa |
| Screw Speed | 20-100 | rpm |
| Shot to Cylinder Size | 30-70 | % |
| Source GMD,last updated:2000/01/05 | ||
Noryl* Resin PPO PX1390
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.