- 产 品：PPO PKN4775 食品级,不透明,高热量,高性能
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Noryl* Food & Water Contact Resin
Food, Water, Medical Solutions
Modified amorphous blends of PPO* resin (polyphenylene ether) and polystyrenes.
Noryl* Resin PKN4775 英文物性表
PPE+PS blend. Opaque. FDA compliant in limited colors. High heat. Modulus at elevated temperature. Good ESCR performance. Thin wall extrusion and injection molding. Typical applications include packaging for high performance applications.
Property
TYPICAL PROPERTIES(1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 520 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 480 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,50mm/min | 5.1 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 35 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 21600 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 800 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 22500 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,50mm/min | 51 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 47 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 4.1 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 29.3 | % | ISO 527 |
| Tensile Modulus,1mm/min | 2120 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 82 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 2160 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 27 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 16 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 404 | cm-kgf | ASTM D 3763 |
| Izod Impact,notched 80*10*4 +23℃ | 20 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 11 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 19 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate B/50 | 142 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2mm,unannealed | 138 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 122 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 9.20E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,xflow | 9.50E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 40℃,flow | 9.20E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 9.50E-05 | 1/℃ | ISO 11359-2 |
| Ball Pressure Test,75℃ +/- 2℃ | N/A | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/50 | 142 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 144 | ℃ | ISO 306 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 122 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.05 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm (5) | 0.5-0.8 | % | SABIC Method |
| Melt Flow Rate,300℃/5.0 kgf | 15.3 | g/10 min | ASTM D 1238 |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.25 | % | ISO 62 |
| Moisture Absorption (23℃ / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate,MVR at 300℃/5.0 kg | 14 | cm³/10 min | ISO 1133 |
| Source GMD,last updated:2004/11/30 | |||
| Parameter Sheet Extrusion | Value | Unit |
| Drying Temperature | 70-80 | ℃ |
| Drying Time | 2-4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0 | % |
| Melt Temperature | 265-275 | ℃ |
| Barrel-Zone 1 Temperature | 205-225 | ℃ |
| Barrel-Zone 2 Temperature | 215-240 | ℃ |
| Barrel-Zone 3 Temperature | 240-265 | ℃ |
| Barrel-Zone 4 Temperature | 240-265 | ℃ |
| Adapter Temperature | 240-265 | ℃ |
| Die Temperature | 240-265 | ℃ |
| Roll Stack Temp-Top | 105-120 | ℃ |
| Roll Stack Temp-Middle | 105-120 | ℃ |
| Roll Stack Temp-Bottom | 105-120 | ℃ |
| Source GMD,last updated:2004/11/30 | ||
• Use lower process temperatures when material is let-down.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.