PPO GFN2 玻纤20%增强,吸水率,水解稳定,尺寸稳定
  • 产 品:PPO GFN2 玻纤20%增强,吸水率,水解稳定,尺寸稳定
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Noryl* Food & Water Contact Resin
Food, Water, Medical Solutions
Modified amorphous blends of PPO* resin (polyphenylene ether) and polystyrenes.

Noryl* Resin GFN2 英文物性表
PPE+PS blend. 20% Glass reinforced. UL746C F1. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings and impellers, valve components and others.

Property
TYPICAL PROPERTIES(1)

MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 910 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.6 % ASTM D 638
Tensile Modulus,5mm/min 63200 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1630 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 59100 kgf/cm² ASTM D 790
Hardness,Rockwell L 106 - ASTM D 785
Tensile Stress,break,5mm/min 97 MPa ISO 527
Tensile Strain,break,5mm/min 2.5 % ISO 527
Tensile Modulus,1mm/min 7070 MPa ISO 527
Flexural Stress,yield,2mm/min 167 MPa ISO 178
Flexural Modulus,2mm/min 6540 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 66 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 12 cm-kgf/cm ASTM D 256
Izod Impact,notched,-40℃ 9 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 230 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*4 +23℃ 11 kJ/m² ISO 180/1A
Charpy Impact,notched,23℃ 11 kJ/m² ISO 179/2C
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 140 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 135 ASTM D 648
HDT,0.45 MPa,6.4mm,unannealed 143 ASTM D 648
HDT,1.82 MPa,6.4mm,unannealed 137 ASTM D 648
CTE,-40℃ to 40℃,flow 2.89E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.26E-05 1/℃ ASTM E 831
Vicat Softening Temp,Rate B/50 143 ISO 306
Vicat Softening Temp,Rate B/120 146 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 143 ISO 75/Be
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm 137 ISO 75/Ae
Relative Temp Index,Elec 90 UL 746B
Relative Temp Index,Mech w/impact 90 UL 746B
Relative Temp Index,Mech w/o impact 90 UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Water Absorption,24 hours 0.06 % ASTM D 570
Mold Shrinkage,flow,3.2mm(5) 0.2-0.5 % SABIC Method
Melt Flow Rate,300℃/5.0 kgf 9 g/10 min ASTM D 1238
Melt Volume Rate,MVR at 300℃/5.0 kg 8 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Dielectric Strength,in oil,3.2mm 16.5 kV/mm ASTM D 149
Relative Permittivity,50/60 Hz 2.86 - ASTM D 150
Dissipation Factor,50/60 Hz 0.0008 - ASTM D 150
Arc Resistance,Tungsten {PLC} 7 PLC Code ASTM D 495
Hot Wire Ignition {PLC) 4 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 4 PLC Code UL 746A
High Ampere Arc Ign,surface {PLC} 4 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized,94HB Flame Class Rating(3) 1.47 mm UL 94
Oxygen Index(LOI) 26 % ASTM D 2863
UV-light,water exposure/immersion F1 - UL 746C
Source GMD,last updated:2004/05/11
Parameter Injection Molding Value Unit
Drying Temperature 110-120
Drying Time 3-4 hrs
Drying Time(Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 300-325
Nozzle Temperature 300-325
Front-Zone 3 Temperature 290-325
Middle-Zone 2 Temperature 275-320
Rear-Zone 1 Temperature 265-315
Mold Temperature 80-110
Back Pressure 0.3-0.7 MPa
Screw Speed 20-100 rpm
Shot to Cylinder Size 30-70 %
Source GMD,last updated:2004/05/11

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.