PPO FN215X 发泡树脂,生产率改进
  • 产 品:PPO FN215X 发泡树脂,生产率改进
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Noryl* Foam Resin
Light, Stiff, Energy Absorbing
Foamable amorphous resins of PPO* resin (polyphenylene ether) and polystyrene

Noryl* Resin FN215X 英文物性表
Structural foam resin. 170F (77C) HDT. Improved reliability and productivity. All values at 20% weight reduction.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit  Standard 
FOAM-MECHANICAL 6.4mm Wt Reduction 20 % -
Tensile Stress,yield,6.35mm 290 kgf/cm² ASTM D 638
Tensile Strain,break,6.35mm 12 % ASTM D 638
Flexural Stress,yield,6.4mm 620 kgf/cm² ASTM D 790
Flexural Modulus,6.4mm 19400 kgf/cm² ASTM D 790
IMPACT Value Unit  Standard 
FOAM-IMPACT 6.4mm Wt Reduction 20 % -
Izod Impact,unnotched,23℃,6.4mm 20 cm-kgf/cm ASTM D 4812
Instrumented Impact Energy @ peak,23℃ 111 cm-kgf ASTM D 3763
Instrumented Impact Energy @ peak,-30 33 cm-kgf ASTM D 3763
THERMAL Value Unit  Standard 
FOAM-THERMAL 6.4mm Wt Reduction 20 % -
HDT,0.45 MPa,6.4mm,unannealed 88 ASTM D 648
HDT,1.82 MPa,6.4mm,unannealed 76 ASTM D 648
Relative Temp Index,Elec 85 UL 746B
Relative Temp Index,Mech w/impact 85 UL 746B
Relative Temp Index,Mech w/o impact 85 UL 746B
PHYSICAL Value Unit  Standard 
FOAM-PHYSICAL 6.4mm Wt Reduction 20 % -
Specific Gravity 1.1 - ASTM D 792
Specific Gravity,foam molded 0.88 - ASTM D 792
Water Absorption,24 hours 0.07 % ASTM D 570
Water Absorption,equilibrium,23C 0.17 % ASTM D 570
Mold Shrinkage,flow,6.4mm(5) 0.6-0.8 % SABIC Method
ELECTRICAL Value Unit  Standard 
Surface Resistivity >1.E+17 Ohm ASTM D 257
Dielectric Strength,in oil,1.6mm 12 kV/mm ASTM D 149
Relative Permittivity,1 MHz 2.2 - ASTM D 150
Dissipation Factor,1 MHz 0.0044 - ASTM D 150
Arc Resistance,Tungsten {PLC} 6 PLC Code ASTM D 495
High Voltage Arc Track Rate {PLC} 4 PLC Code UL 746A
Comparative Tracking Index(UL){PLC} 1 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit  Standard 
FOAM-Flame Class Minimum Density 0.85 g/cm³ -
UL Recognized,94V-1 Flame Class Rating(3) 2.99 mm UL 94
UL Recognized,94V-0 Flame Class Rating(3) 5.99 mm UL 94
UL Recognized,94-5VA Rating(3) 3.91 mm UL 94
Radiant Panel Listing YES - UL Tested
UV-light,water exposure/immersion F1 - UL 746C
Source GMD,last updated:1991/09/25
Parameter Structural Foam Molding Value Unit 
Blowing Agent,Physical System Nitrogen Gas -
Concentration Range(Blowing Agent) 1-3 %
Recommended Concentration(Blowing Agent) 2 %
Drying Temperature(Resin) 70-80
Drying Time(Resin) 2-4 hrs
Drying Time(Resin,Cumulative) 8 hrs
Melt Temperature 270-310
Nozzle Temperature 270-305
Front Temperature 270-305
Middle Temperature 270-305
Rear Temperature 230-260
Mold Temperature 25-55
Source GMD,last updated:1991/09/25

• Drying is not required/recommended.

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.