- 产 品：PPO FN170X 发泡树脂
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Noryl* Foam Resin
Light, Stiff, Energy Absorbing
Foamable amorphous resins of PPO* resin (polyphenylene ether) and polystyrene
Noryl* Resin FN170X 英文物性表
Foamable resin. All properties at 10% density reduction; 0.250" thick test specimens.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| FOAM-MECHANICAL 6.4mm Wt Reduction | 10 | % | - |
| Tensile Stress,yield,6.35mm | 290 | kgf/cm² | ASTM D 638 |
| Tensile Stress,break,6.35mm | 290 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yield,6.35mm | 5.7 | % | ASTM D 638 |
| Tensile Strain,break,6.35mm | 13.1 | % | ASTM D 638 |
| Flexural Stress,yield,6.4mm | 670 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,6.4mm | 21700 | kgf/cm² | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| FOAM-IMPACT 6.4mm Wt Reduction | 10 | % | - |
| Izod Impact,unnotched,23℃,6.4mm | 28 | cm-kgf/cm | ASTM D 4812 |
| Instrumented Impact Energy @ peak,23℃ | 587 | cm-kgf | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| FOAM-THERMAL 6.4mm Wt Reduction | 10 | % | - |
| HDT,0.45 MPa,6.4mm,unannealed | 89 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,6.4mm,unannealed | 78 | ℃ | ASTM D 648 |
| Relative Temp Index,Elec | 85 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 85 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 85 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| FOAM-PHYSICAL 6.4mm Wt Reduction | 10 | % | - |
| Specific Gravity ppo | 1.11 | - | ASTM D 792 |
| Specific Gravity,foam molded | 1 | - | ASTM D 792 |
| Water Absorption,24 hours | 0.06 | % | ASTM D 570 |
| Mold Shrinkage,flow,6.4mm (5) | 0.6-0.8 | % | SABIC Method |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance,Tungsten {PLC} | 6 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| High Ampere Arc Ign,surface {PLC} | 2 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| FOAM-Flame Class Minimum Density | 1 | g/cm³ | - |
| UL Recognized,94V-1 Flame Class Rating (3) | 2.99 | mm | UL 94 |
| UL Recognized,94-5VA Rating (3) | 4.69 | mm | UL 94 |
| Radiant Panel Listing | YES | - | UL Tested |
| UV-light, water exposure/immersion | F2 | - | UL 746C |
| Source GMD, last updated:1994/01/07 | |||
| Parameter Structural Foam Molding | Value | Unit |
| Blowing Agent,Physical System | Nitrogen Gas | - |
| Concentration Range (Blowing Agent) | 1-3 | % |
| Recommended Concentration (Blowing Agent) | 2 | % |
| Drying Temperature (Resin) | 70-80 | ℃ |
| Drying Time (Resin) | 2-4 | hrs |
| Drying Time (Resin,Cumulative) | 8 | hrs |
| Melt Temperature | 270-310 | ℃ |
| Nozzle Temperature | 270-305 | ℃ |
| Front Temperature | 270-305 | ℃ |
| Middle Temperature | 270-305 | ℃ |
| Rear Temperature | 230-260 | ℃ |
| Mold Temperature | 25-55 | ℃ |
| Source GMD,last updated:1994/01/07 | ||
• Drying is not required/recommended.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.