- 产 品：PPO WCV063 无卤,挤出级,汽车电线涂层应用
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Noryl* Flexible Noryl Resin
Flexible and non Halogenated
Flexible materials comprised of PPO™ resin (polyphenylene ether) and TPE's (thermoplastic elastomers) are commonly used for wire, cable and jacket insulation.
Noryl* Resin PPO WCV063 英文物性表
Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,50mm/min | 280 | kJ/m² | ASTM D 638 |
| Tensile Stress,brk,Type I,50mm/min | 280 | kJ/m² | ASTM D 638 |
| Tensile Strain,brk,Type I,50mm/min | 90 | % | ASTM D 638 |
| Tensile Modulus,50mm/min | 8500 | kJ/m² | ASTM D 638 |
| Flexural Modulus,1.3mm/min,50mm span | 7300 | kJ/m² | ASTM D 790 |
| Hardness,Shore D,10S reading | 63 | - | ASTM D 2240 |
| Tensile Stress,yield | 25 | MPa | ISO 527 |
| Tensile Stress,break,50mm/min | 25 | MPa | ISO 527 |
| Tensile Strain,yield,50mm/min | 20 | % | ISO 527 |
| Tensile Strain,break,50mm/min | 50 | % | ISO 527 |
| Tensile Modulus,1mm/min | 690 | MPa | ISO 527 |
| Flexural Modulus | 790 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,notched,23℃ | 57 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 17 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched 80*10*4 +23℃ | 37 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 82 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 56 | ℃ | ASTM D 648 |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 66 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.03 | - | ASTM D 792 |
| Melt Flow Rate,280℃5.0 kgf | 33 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Relative Permittivity,1 GHz | 2.47 | - | ASTM D 150 |
| Dissipation Factor,1 GHz | 0.0032 | - | ASTM D 150 |
| Source GMD,last updated:2009/11/03 | |||
| Parameter Wire Coating Extrusion | Value | Unit |
| Drying Temperature | 80-100 | ℃ |
| Drying Time | 4-6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Extruder Length/Diameter Ratio (L/D) | >24:1 | - |
| Compression Ratio | 2;1-3:1 | - |
| Screw Speed | 5-60 | rpm |
| Feed Zone Temperature | 200-260 | ℃ |
| Middle Zone Temperatures | 270-300 | ℃ |
| Head Zone Temperature | 280-300 | ℃ |
| Neck Temperature | 280-300 | ℃ |
| Cross-head Temperature | 280-300 | ℃ |
| Die Temperature | 280-300 | ℃ |
| Melt Temperature | 280-300 | ℃ |
| Conductor Pre-heat Temperature | 100-150 | ℃ |
| Screen Pack | 60/200/60 | - |
| Cooling Water Air Gap | 100-1000 | mm |
| Water Bath Temperature | 15-30 | ℃ |
| Source GMD, last updated:2009/11/03 | ||
DRYING
• Dehumidification or vacuum oven dryers are recommended
ADDITIONAL SUGGESTIONS
• On-size dies are recommended
• Extrusion equipment should be purged thoroughly before shutting down
• A screw with mixing section can be used if properly designed to prevent excessive heat build-up
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、 Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.