Noryl* Flexible Noryl Resin
Flexible and non Halogenated
Flexible materials comprised of PPO™ resin (polyphenylene ether) and TPE's (thermoplastic elastomers) are commonly used for wire, cable and jacket insulation.
Noryl* Resin PPO WCP821 英文物性表
Flexible Noryl* injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in over-molding applications such as plugs, strain relief's, and connectors. UL 94-V0 performance with good processability.
Property
TYPICAL PROPERTIES (1)
MECHANICAL | Value | Unit | Standard |
Tensile Stress,brk,Type I,50mm/min | 100 | kgf/cm² | ASTM D 638 |
Tensile Strain,brk,Type I,50mm/min | 125 | % | ASTM D 638 |
Flexural Modulus,12.5mm/min,100mm span | 1100 | kgf/cm² | ASTM D 790 |
Hardness,Shore A,30S reading | 82 | - | ASTM D 2240 |
Tensile Stress,break,50mm/min | 10 | MPa | ISO 527 |
Tensile Strain,break,50mm/min | 115 | % | ISO 527 |
Flexural Modulus,12.5mm/min | 130 | MPa | ISO 178 |
Tear strength | 17 | N/mm | ISO 6383 |
IMPACT | Value | Unit | Standard |
Brittleness Temperature | <-40 | ℃ | ASTM D 746 |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.05 | - | ASTM D 792 |
Water Absorption,23℃/48hrs | 0.1 | % | ASTM D 570 |
Mold Shrinkage,flow,24 hrs(5) | 0.48 | % | ASTM D 955 |
Mold Shrinkage,xflow,24 hrs(5) | 1.09 | % | ASTM D 955 |
Melt Flow Rate,210℃/5 kgf | 31 | g/10 min | ASTM D 1238 |
Melt Flow Rate,250℃/2.16 kgf | 33 | g/10 min | ASTM D 1238 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 2.20E+15 | Ohm-cm | ASTM D 257 |
Dielectric strength in oil,2.0mm | 25 | kV/mm | IEC 60243-1 |
Relative Permittivity,1 MHz | 2.7 | - | IEC 60250 |
Dissipation Factor,1 MHz | 0.004 | - | IEC 60250 |
Comparative ppoTracking Index | 600 | V | IEC 60112 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized,94V-0 Flame Class Rating(3) | 5 | mm | UL 94 |
Smoke Density on 0.5mm plaque,Non-flame,Ds,max | 70 | - | ASTM E 662 |
Smoke Density on 0.5mm plaque,Flame,Ds,max | 90 | - | ASTM E 662 |
Glow Wire Flammability Index 850℃,passes at | 3 | mm | IEC 60695-2-12 |
Glow Wire Ignitability Temperature,3.0mm | 800 | ℃ | IEC 60695-2-13 |
Oxygen Index(LOI) | 25 | % | ISO 4589 |
Source GMD,last updated:2007/07/13 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 60-80 | ℃ |
Drying Time | 4-6 | hrs |
Drying Time(Cumulative) | 8 | hrs |
Maximum Moisture Content | 0.01 | % |
Melt Temperature | 220-250 | ℃ |
Nozzle Temperature | 220-250 | ℃ |
Front-Zone 3 Temperature | 220-250 | ℃ |
Middle-Zone 2 Temperature | 210-240 | ℃ |
Rear-Zone 1 Temperature | 180-220 | ℃ |
Mold Temperature | 40-60 | ℃ |
Back Pressure | 3-10 | MPa |
Screw Speed | 30-80 | rpm |
Shot to Cylinder Size | 30-70 | % |
Vent Depth | 0.03-0.05 | mm |
Source GMD,last updated:2007/07/13 |
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、 Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
关健字:Noryl* Resin PPO WCP821