PPO SE1GFN1 玻纤10%增强,无溴氯阻燃,尺寸稳定
  • 产 品:PPO SE1GFN1 玻纤10%增强,无溴氯阻燃,尺寸稳定
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Noryl* FR Reinforced Resin
Flame Retardant, Heat Resistant
General purpose, reinforced modified amorphous blends of PPO* resin (polyphenylene ether) and polystyrene or high-impact polystyrene with non-brominated, non-chlorinated flame retardants.

Noryl* Resin SE1GFN1 英文物性表
PPE+PS blend. 10% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. RTI 110/105/110. Dielectric strength. Dimensional stability. Suitable for E/E applications.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit  Standard 
Tensile Stress,brk,Type I,5mm/min 750 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 5 % ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 1220 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 40700 kgf/cm² ASTM D 790
Hardness,Rockwell L 104 - ASTM D 785
IMPACT Value Unit  Standard 
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
Izod Impact,notched,-40℃ 7 cm-kgf/cm ASTM D 256
THERMAL Value Unit  Standard 
Vicat Softening Temp,Rate B/50 147 ASTM D 1525
HDT,1.82 MPa,6.4mm,unannealed 131 ASTM D 648
Relative Temp Index,Elec 110 UL 746B
Relative Temp Index,Mechw/impact 105 UL 746B
Relative Temp Index,Mech w/o impact 110 UL 746B
PHYSICAL Value Unit  Standard 
Specific Gravity 1.16 - ASTM D 792
Water Absorption,24 hours 0.07 % ASTM D 570
Water Absorption,equilibrium,23C 0.22 % ASTM D 570
Mold Shrinkage,flow,3.2mm (5) 0.3-0.5 % SABIC Method
ELECTRICAL Value Unit  Standard 
Volume Resistivity 1E+15 Ohm-cm ASTM D 257
Relative Permittivity,50/60 Hz 3 - ASTM D 150
Relative Permittivity,1 MHz 3 - ASTM D 150
Dissipation Factor,50/60 Hz 0.0017 - ASTM D 150
Dissipation Factor,1 MHz 0.0016 - ASTM D 150
Hot Wire Ignition {PLC) 1 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 4 PLC Code UL 746A
High Ampere Arc Ign,surface {PLC} 2 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 2 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit  Standard 
UL Recognized,94V-1 Flame Class Rating (3) 1.47 mm UL 94
Oxygen Index (LOI) 33.9 % ASTM D 2863
Source GMD,last updated:1999/12/29
Parameter Injection Molding Value Unit 
Drying Temperature 105-110
Drying Time 3-4 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 280-310
Nozzle Temperature 280-310
Front-Zone 3 Temperature 270-310
Middle-Zone 2 Temperature 260-305
Rear-Zone 1 Temperature 250-300
Mold Temperature 75-105
Back Pressure 0.3-0.7 MPa
Screw Speed 20-100 rpm
Shot to Cylinder Size 30-70 %
Source GMD,last updated:1999/12/29

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、 Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.