快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
塑胶原料报价
- 产 品：PPO PX1005X 注塑阻燃级
- 产 地：noryl(美国GE)
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
上一篇：PPO PC180X 注塑阻燃级 下一篇：PPO N190X 注塑阻燃级
noryl PPO 注塑级 阻燃 PX1005X
Noryl PPO PX1005X物性
PPE+PS合金,无溴无氯阻燃,UL94 V0/5VA.优异的介电强度,用于电子/电气市场的室内/室外应用.
|
Property
|
|
TYPICAL PROPERTIES (1)
|
||||
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
560
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
420
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
3.1
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
17
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
24400
|
kgf/cm²
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
810
|
kgf/cm²
|
ASTM D 790
|
|
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span
|
810
|
kgf/cm²
|
ASTM D 790
|
|
|
Flexural Modulus
|
24700
|
kgf/cm²
|
ASTM D 790
|
|
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
22400
|
kgf/cm²
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
53
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
43
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
2.8
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
12.5
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2460
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
76
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2480
|
MPa
|
ISO 178
|
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
|
Izod Impact, unnotched, 23°C
|
119
|
cm-kgf/cm
|
ASTM D 4812
|
|
|
Izod Impact, notched, 23°C
|
30
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
9
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
22
|
kJ/m²
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
23
|
kJ/m²
|
ISO 179/1eA
|
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
|
Vicat Softening Temp, Rate B/50
|
107
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
84
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
72
|
°C
|
ASTM D 648
|
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
88
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
78
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
8.9E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
1.03E-04
|
1/°C
|
ASTM E 831
|
|
|
Vicat Softening Temp, Rate B/50
|
94
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
97
|
°C
|
ISO 306
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
88
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
75
|
°C
|
ISO 75/Ae
|
|
|
Relative Temp Index, Elec
|
95
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
80
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
95
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
|
Specific Gravity
|
1.12
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Mold Shrinkage on Tensile Bar, xflow (2)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 280°C/5.0 kgf
|
37
|
g/10 min
|
ASTM D 1238
|
|
|
Melt Volume Rate, MVR at 280°C/5.0 kg
|
37
|
cm³/10 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
|
Volume Resistivity
|
3.3E+16
|
Ohm-cm
|
ASTM D 257
|
|
|
Surface Resistivity
|
>1.E+16
|
Ohm
|
ASTM D 257
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
17.7
|
kV/mm
|
ASTM D 149
|
|
|
Relative Permittivity, 50/60 Hz
|
2.67
|
-
|
ASTM D 150
|
|
|
Relative Permittivity, 1 MHz
|
2.53
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 50/60 Hz
|
0.012
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 1 MHz
|
0.0026
|
-
|
ASTM D 150
|
|
|
Arc Resistance, Tungsten {PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
|
Hot Wire Ignition {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
|
High Voltage Arc Track Rate {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.01
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.47
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VA Rating (3)
|
2.99
|
mm
|
UL 94
|
|
|
UV-light, water exposure/immersion
|
F1
|
-
|
UL 746C
|
|
|
Processing
|
|
Parameter
|
||
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
75 - 80
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
250 - 275
|
°C
|
|
Nozzle Temperature
|
250 - 275
|
°C
|
|
Front - Zone 3 Temperature
|
240 - 275
|
°C
|
|
Middle - Zone 2 Temperature
|
225 - 270
|
°C
|
|
Rear - Zone 1 Temperature
|
215 - 265
|
°C
|
|
Mold Temperature
|
55 - 75
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
20 - 100
|
rpm
|
|
Shot to Cylinder Size
|
30 - 70
|
%
|
|
Vent Depth
|
0.038 - 0.051
|
mm
|