快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
- 产 品：PPE PPX830 玻纤30%增强,尺寸稳定,耐化学级
- 产 地：沙伯基础创新
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
Noryl PPX* Resin
Ready for Your Needs
Noryl PPX* resins are modified polyphenylene ether (PPE) / polypropylene (PP) resin blends that offer excellent melt strength and processibility, dimensional stability at temperature extremes, a wide range of stiffness, chemical resistance, and hydrolytic stability. Grades include recyclable unfilled and filled, high elongation, impact modified, and high stiffness.
Noryl PPX* Resin PPX830 数据表
Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30% Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus of 7600 MPa; this grade has been developed for application where dimension stability, temperature and chemical resistance could be required. Noryl PPX830 is an opaque material available in limited colors only.
Property
TYPICAL PROPERTIES (1)
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5mm/min | 1020 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5mm/min | 1020 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5mm/min | 2.9 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 101 | % | ASTM D 638 |
| Tensile Modulus,5mm/min | 77400 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3mm/min,50mm span | 1460 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 67300 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5mm/min | 98 | MPa | ISO 527 |
| Tensile Stress,break,5mm/min | 98 | MPa | ISO 527 |
| Tensile Strain,yield,5mm/min | 3.2 | % | ISO 527 |
| Tensile Strain,break,5mm/min | 3.2 | % | ISO 527 |
| Tensile Modulus,1mm/min | 7700 | MPa | ISO 527 |
| Flexural Stress,yield,2mm/min | 141 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 7100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 66 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 9 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy,23℃ | 152 | cm-kgf | ASTM D 3763 |
| Instrumented Impact Total Energy,-30℃ | 101 | cm-kgf | ASTM D 3763 |
| Izod Impact,unnotched 80*10*4 +23℃ | 42 | kJ/m² | ISO 180/1U |
| Izod Impact,unnotched 80*10*4 -30℃ | 42 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 10 | kJ/m² | ISO 180/1A |
| Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm | 39 | kJ/m² | ISO 179/1eU |
| Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm | 36 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2mm,unannealed | 166 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 156 | ℃ | ASTM D 648 |
| CTE,-40℃ to 95℃,flow | 2.50E-05 | 1/℃ | ASTM E 831 |
| CTE,-40℃ to 95℃,xflow | 1.30E-04 | 1/℃ | ASTM E 831 |
| CTE,-30℃ to 80℃,flow | 2.50E-05 | 1/℃ | ISO 11359-2 |
| CTE,-30℃ to 80℃,xflow | 1.20E-04 | 1/℃ | ISO 11359-2 |
| Ball Pressure Test,125℃ +/- 2℃ | Passes | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate B/120 | 150 | ℃ | ISO 306 |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 168 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 153 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2mm(5) | 0.2-0.25 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2mm(5) | 0.4-0.6 | % | SABIC Method |
| Melt Flow Rate,280℃/5.0 kgf | 6 | g/10 min | ASTM D 1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate,MVR at 280℃/5.0 kg | 6 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized,94HB Flame Class Rating(3) | 1 | mm | UL 94 |
| Glow Wire Flammability Index 650℃,passes at | 3 | mm | IEC 60695-2-12 |
| Source GMD,last updated:2008/08/19 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 65-75 | ℃ |
| Drying Time | 2-4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260-300 | ℃ |
| Nozzle Temperature | 260-300 | ℃ |
| Front-Zone 3 Temperature | 255-290 | ℃ |
| Middle-Zone 2 Temperature | 250-290 | ℃ |
| Rear-Zone 1 Temperature | 245-290 | ℃ |
| Hopper Temperature | 60-80 | ℃ |
| Mold Temperature | 40-65 | ℃ |
| Source GMD,last updated:2008/08/19 | ||
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.