PPE GTX975 耐高温,导电静电喷涂,矿物填充材料
  • 产 品:PPE GTX975 耐高温,导电静电喷涂,矿物填充材料
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Noryl GTX* Resin
Strenth, Paintability and Lightweight
Noryl* GTX resins are modified polyphenylene ether (PPE) / polyamide (PA) resin blends that combine PPE's dimensional stability, low water absorption and heat resistance with PA's chemical resistance and flow characteristics. Grades include flame retardant, filled, conductive, blowmolding/extrusion in addition to injection molding grades, ultra high stiffness, automotive, and high flow.

Noryl GTX* Resin GTX975 数据表
NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting in an unique way.

Property
TYPICAL PROPERTIES (1)
 

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 700 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 690 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 3.5 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 4.5 % ASTM D 638
Tensile Modulus,5mm/min 45300 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 1150 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 40700 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 65 MPa ISO 527
Tensile Stress,break,5mm/min 65 MPa ISO 527
Tensile Strain,yield,5mm/min 3.5 % ISO 527
Tensile Strain,break,5mm/min 4 % ISO 527
Tensile Modulus,1mm/min 4200 MPa ISO 527
Flexural Stress,break,2mm/min 110 MPa ISO 178
Flexural Modulus,2mm/min 4000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 3 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 30 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 40 kJ/m² ISO 180/1U
Izod Impact,unnotched 80*10*4 -30℃ 35 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 4 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 4 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 3 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 3 kJ/m² ISO 179/1eA
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm 40 kJ/m² ISO 179/1eU
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm 35 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 215 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 210 ASTM D 648
CTE,-40℃ to 40℃,flow 5.40E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 6.00E-05 1/℃ ASTM E 831
CTE,23℃ to 60℃,flow 5.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 6.50E-05 1/℃ ISO 11359-2
Vicat Softening Temp,Rate B/50 195 ISO 306
Vicat Softening Temp,Rate B/120 200 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 185 ISO 75/Be
PHYSICAL Value Unit Standard
Specific Gravity 1.25 - ASTM D 792
Mold Shrinkage,flow,3.2mm(5) 0.8-1.2 % SABIC Method
Melt Flow Rate,280℃/5.0 kgf 15 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 3.5 % ISO 62
Moisture Absorption(23℃/50% RH) 1.1 % ISO 62
Melt Volume Rate,MVR at 280℃/5.0 kg 10 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+03-1.E+04 Ohm-cm SABIC Method
Source GMD,last updated:2007/11/26
Parameter Injection Molding Value Unit
Drying Temperature 100-110
Drying Time 2-3 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 300-320
Nozzle Temperature 280-300
Front-Zone 3 Temperature 300-320
Middle-Zone 2 Temperature 280-300
Rear-Zone 1 Temperature 260-280
Hopper Temperature 80-100
Mold Temperature 100-120
Source GMD,last updated:2007/11/26

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.