PPE GTX934 改善加工性能和热老化性能
  • 产 品:PPE GTX934 改善加工性能和热老化性能
  • 产 地:沙伯基础创新
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

Noryl GTX* Resin
Strenth, Paintability and Lightweight
Noryl* GTX resins are modified polyphenylene ether (PPE) / polyamide (PA) resin blends that combine PPE's dimensional stability, low water absorption and heat resistance with PA's chemical resistance and flow characteristics. Grades include flame retardant, filled, conductive, blowmolding/extrusion in addition to injection molding grades, ultra high stiffness, automotive, and high flow.

Noryl GTX* Resin GTX934 数据表
NORYL GTX934 is an unfilled GTX grade with improved processability and heat ageing performance.

Property
TYPICAL PROPERTIES (1)

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 660 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 560 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 5 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 60 % ASTM D 638
Tensile Modulus,50mm/min 23400 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 960 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 23900 kgf/cm² ASTM D 790
Tensile Stress,yield,50mm/min 65 MPa ISO 527
Tensile Stress,break,50mm/min 55 MPa ISO 527
Tensile Strain,yield,50mm/min 4.5 % ISO 527
Tensile Strain,break,50mm/min 25 % ISO 527
Tensile Modulus,1mm/min 2400 MPa ISO 527
Flexural Stress,yield,2mm/min 90 MPa ISO 178
Flexural Modulus,2mm/min 2200 MPa ISO 178
Hardness,H358/30 85 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact,notched,23℃ 22 cm-kgf/cm ASTM D 256
Izod Impact,notched,-30℃ 10 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy,23℃ 611 cm-kgf ASTM D 3763
Izod Impact,notched 80*10*4 +23℃ 20 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -30℃ 10 kJ/m² ISO 180/1A
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm 20 kJ/m² ISO 179/1eA
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm 10 kJ/m² ISO 179/1eA
THERMAL Value Unit Standard
Vicat Softening Temp,Rate B/50 205 ASTM D 1525
HDT,0.45 MPa,3.2mm,unannealed 190 ASTM D 648
CTE,-40℃ to 40℃,flow 7.50E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 8.50E-05 1/℃ ASTM E 831
Thermal Conductivity 0.23 W/m-℃ ISO 8302
CTE,23℃ to 60℃,flow 8.00E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 7.00E-05 1/℃ ISO 11359-2
Ball Pressure Test,125℃ +/- 2℃ PASSES - IEC 60695-10-2
Vicat Softening Temp,Rate A/50 250 ISO 306
Vicat Softening Temp,Rate B/50 200 ISO 306
Vicat Softening Temp,Rate B/120 205 ISO 306
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm 190 ISO 75/Be
PHYSICAL Value Unit Standard
Specific Gravity 1.09 - ASTM D 792
Mold Shrinkage on Tensile Bar,flow (2) (5) 1.6-2 % SABIC Method
Mold Shrinkage,flow,3.2mm (5) 1.4-1.7 % SABIC Method
Mold Shrinkage,xflow,3.2mm (5) 1.1-1.4 % SABIC Method
Melt Flow Rate,280℃/5.0 kgf 13 g/10 min ASTM D 1238
Density 1.09 g/cm³ ISO 1183
Water Absorption,(23℃/sat) 3.5 % ISO 62
Moisture Absorption (23℃/50% RH) 1.21 % ISO 62
Melt Volume Rate,MVR at 280℃/5.0 kg 13 cm³/10 min ISO 1133
Source GMD,last updated:2007/06/25
Parameter Injection Molding Value Unit 
Drying Temperature 100-120
Drying Time 2-3 hrs
Maximum Moisture Content 0.07 %
Melt Temperature 290-320
Nozzle Temperature 280-310
Front-Zone 3 Temperature 290-320
Middle-Zone 2 Temperature 280-300
Rear-Zone 1 Temperature 260-280
Hopper Temperature 60-80
Mold Temperature 80-120
Source GMD,last updated:2007/06/25

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.