快速查找
主营塑料
产品推荐
- ⊕PPS OL003A 含玻璃纤维,聚四氟乙
- ⊕PBT 420SE0 玻纤30%增强,阻燃级
- ⊕PBT 310SE0 非增强型,PBT阻燃树脂
- ⊕PP HJ730 高流动,高钢性,高耐热
- ⊕PP FB71U6 耐热级,抗UV,阻燃级
- ⊕PA6 73G30L NC010 玻璃纤维30%增
- ⊕PA66 70G43L NC010 玻璃纤维43%增
- ⊕PA66 70G33L NC010 玻璃纤维33%增
- ⊕PA66 70G30L NC010 玻璃纤维30%增
- ⊕PA66 80G33L NC010 玻纤33%增强,
- ⊕PA66 FR50 NC010A 玻纤25%增强,阻
- ⊕POM 900P NC010 低粘度,热稳定,低
- ⊕POM 500P NC010 中高粘,热稳定,低
- ⊕POM 100P NC010 高粘度,韧性好,热
- ⊕PBT SK605 NC010 玻璃纤维30%增强
- ⊕PA66 1300G 玻纤增强级
联系我们
Noryl GTX* Resin
Strenth, Paintability and Lightweight
Noryl* GTX resins are modified polyphenylene ether (PPE) / polyamide (PA) resin blends that combine PPE's dimensional stability, low water absorption and heat resistance with PA's chemical resistance and flow characteristics. Grades include flame retardant, filled, conductive, blowmolding/extrusion in addition to injection molding grades, ultra high stiffness, automotive, and high flow.
Noryl GTX* Resin GTX8721 数据表
Noryl GTX GTX8721 resin is a glass and talc filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, conductivity, and low warpage. This grade can be electrostatically painted or powder coated without the need for conductive primer.
Property
TYPICAL PROPERTIES (1)
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,5mm/min | 1470 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,5mm/min | 1470 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,5mm/min | 2 | % | ASTM D 638 |
Tensile Strain,brk,Type I,5mm/min | 5 | % | ASTM D 638 |
Tensile Modulus,5mm/min | 107000 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3mm/min,50mm span | 2240 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3mm/min,50mm span | 96800 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield,5mm/min | 145 | MPa | ISO 527 |
Tensile Stress,break,5mm/min | 145 | MPa | ISO 527 |
Tensile Strain,yield,5mm/min | 2 | % | ISO 527 |
Tensile Strain,break,5mm/min | 5 | % | ISO 527 |
Tensile Modulus,1mm/min | 10500 | MPa | ISO 527 |
Flexural Stress,yield,2mm/min | 220 | MPa | ISO 178 |
Flexural Modulus,2mm/min | 9500 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 8 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,-30℃ | 6 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Total Energy,23℃ | 61 | cm-kgf | ASTM D 3763 |
Izod Impact,notched 80*10*4 +23℃ | 7 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 6 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp,Rate B/50 | 220 | ℃ | ASTM D 1525 |
HDT,0.45 MPa,3.2mm,unannealed | 220 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 2.20E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 6.80E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 2.20E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 6.80E-05 | 1/℃ | ISO 11359-2 |
Vicat Softening Temp,Rate B/50 | 215 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 215 | ℃ | ISO 306 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 215 | ℃ | ISO 75/Bf |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.37 | - | ASTM D 792 |
Mold Shrinkage,flow,3.2mm(5) | 0.23-0.28 | % | SABIC Method |
Mold Shrinkage,xflow,3.2mm(5) | 0.64-0.7 | % | SABIC Method |
Melt Flow Rate,280℃/5.0 kgf | 6.8 | g/10 min | ASTM D 1238 |
Density | 1.37 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 4 | % | ISO 62 |
Moisture Absorption(23℃/50% RH) | 1.2 | % | ISO 62 |
Melt Volume Rate,MVR at 280℃/5.0 kg | 5 | cm³/10 min | ISO 1133 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 5.E+02-1.E+04 | Ohm-cm | SABIC Method |
Source GMD,last updated:2008/01/07 |
• Do NOT mix NORYL GTX* resin with other grades of NORYL* resins.
Parameter Injection Molding | Value | Unit |
Drying Temperature | 95-105 | ℃ |
Drying Time | 3-4 | hrs |
Drying Time(Cumulative) | 8 | hrs |
Maximum Moisture Content | 0.07 | % |
Minimum Moisture Content | 0.02 | % |
Melt Temperature | 280-305 | ℃ |
Nozzle Temperature | 280-305 | ℃ |
Front-Zone 3 Temperature | 275-305 | ℃ |
Middle-Zone 2 Temperature | 270-305 | ℃ |
Rear-Zone 1 Temperature | 265-305 | ℃ |
Mold Temperature | 75-120 | ℃ |
Back Pressure | 0.3-1.4 | MPa |
Screw Speed | 20-100 | rpm |
Shot to Cylinder Size | 30-50 | % |
Vent Depth | 0.013-0.038 | mm |
Source GMD,last updated:2008/01/07 |
• Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin.
• Regrind must also be dried. Maximum 25% regrind.
• Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:
• 4-8 hrs at 95℃(200℉), 10 hrs max
• 6-12 hrs at 80℃(175℉), 16 hrs max
• 8-16 hrs at 65℃(150℉), 24 hrs max
• Avoid melt temperature in excess of 300℃(575℉) and residence times over 6-8 minutes (may affect properties and/or appearance).
• Nozzle temperature controls assist in elimination of drool premature freeze-off.
• Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics
1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.