Noryl GTX* Resin
Strenth, Paintability and Lightweight
Noryl* GTX resins are modified polyphenylene ether (PPE) / polyamide (PA) resin blends that combine PPE's dimensional stability, low water absorption and heat resistance with PA's chemical resistance and flow characteristics. Grades include flame retardant, filled, conductive, blowmolding/extrusion in addition to injection molding grades, ultra high stiffness, automotive, and high flow.

Noryl GTX* Resin GTX675 数据表
Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to allow for primer-less electrostatic painting. The mineral content enables the material to be used in structural applications replacing metal or thermoset resins. The material is only available in black.

Property
TYPICAL PROPERTIES (1)

• Do NOT mix NORYL GTX* resin with other grades of NORYL* resins.

• Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin.
• Regrind must also be dried. Maximum 25% regrind.
• Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:
    • 4-8 hrs at 95℃(200℉), 10 hrs max
    • 6-12 hrs at 80℃(175℉), 16 hrs max
    • 8-16 hrs at 65℃(150℉), 24 hrs max
• Avoid melt temperature in excess of 300℃(575℉) and residence times over 6-8 minutes (may affect properties and/or appearance).
• Nozzle temperature controls assist in elimination of drool premature freeze-off.
• Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字：【Noryl GTX* Resin PPE/PA6 GTX675】

PA66 70G30HSLR NC010 玻纤30%,热稳定,抗水解