POM KX96321 包含专有填料.导电聚甲醛树脂
  • 产 品:POM KX96321 包含专有填料.导电聚甲醛树脂
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ STAT-KON™ Compound POM KX96321 塑料物性表

Also known as:LNP™Stat-kon™Compound PDX-K-96321 Product reorder name:KX96321
LNP* Stat-Kon* KX96321 is a compound based on Acetal resin containing Proprietary Fillers. Characteristic of this grade is Conductive.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 470 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 450 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 5 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 13 % ASTM D 638
Tensile Modulus,5mm/min 29100 kgf/cm² ASTM D 638
Flexural Modulus,1.3mm/min,50mm span 27000 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 44 MPa ISO 527
Tensile Stress,break,5mm/min 42 MPa ISO 527
Tensile Strain,yield,5mm/min 4 % ISO 527
Tensile Strain,break,5mm/min 7 % ISO 527
Tensile Modulus,1mm/min 2900 MPa ISO 527
Flexural Stress 71 MPa ISO 178
Flexural Modulus,2mm/min 2600 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 52 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Multiaxial Impact 10 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 40 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 31 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 159 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 106 ASTM D 648
CTE,-30℃ to 30℃,flow 1.04E-04 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 9.50E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 141 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 86 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.5 - ASTM D 792
Density 1.5 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.18 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 3-5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 2-4 % ASTM D 955
Moisture Absorption(23℃/50% RH) 0.19 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 2.E+00-5.E+00 Ohm ASTM D 257
Source GMD,last updated:2011/02/01
Parameter Injection Molding Value Unit
Drying Temperature 65-75
Drying Time 4-6 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.01 %
Melt Temperature 220-250
Nozzle Temperature 220-250
Front-Zone 3 Temperature 220-250
Middle-Zone 2 Temperature 210-240
Rear-Zone 1 Temperature 180-220
Mold Temperature 40-60
Back Pressure 3-10 MPa
Screw Speed 30-80 rpm
Shot to Cylinder Size 30-70 %
Vent Depth 0.03-0.05 mm
Source GMD,last updated:2011/02/01