LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ STAT-KON™ Compound POM KE004 塑料物性表
Also known as:LNP™ Stat-kon™ Compound KC-1004 Product reorder name:KE004
LNP* Stat-kon* KE004 is a compound based on Acetal Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yield | 1230 | kgf/cm² | ASTM D 638 |
Tensile Stress,break | 1230 | kgf/cm² | ASTM D 638 |
Tensile Strain,yield | 1.6 | % | ASTM D 638 |
Tensile Strain,break | 1.6 | % | ASTM D 638 |
Tensile Modulus,50mm/min | 147600 | kgf/cm² | ASTM D 638 |
Flexural Stress | 1540 | kgf/cm² | ASTM D 790 |
Flexural Modulus | 112400 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield | 110 | MPa | ISO 527 |
Tensile Stress,break | 110 | MPa | ISO 527 |
Tensile Strain,yield | 1.4 | % | ISO 527 |
Tensile Strain,break | 1.4 | % | ISO 527 |
Tensile Modulus,1mm/min | 12990 | MPa | ISO 527 |
Flexural Stress | 160 | MPa | ISO 178 |
Flexural Modulus | 11500 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 43 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 4 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Energy @ peak,23℃ | 111 | cm-kgf | ASTM D 3763 |
Multiaxial Impact | 25 | cm-kgf | ISO 6603 |
Izod Impact,unnotched 80*10*4 +23℃ | 25 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,3.2mm,unannealed | 162 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 160 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 6.84E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 3.06E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 6.90E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 3.10E-05 | 1/℃ | ISO 11359-2 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 163 | ℃ | ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 160 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Density | 1.47 | g/cm³ | ASTM D 792 |
Moisture Absorption,50% RH,24 hrs | 0.2 | % | ASTM D 570 |
Mold Shrinkage,flow,24 hrs(5) | 0.6-0.8 | % | ASTM D 955 |
Mold Shrinkage,xflow,24 hrs(5) | 1.6-1.8 | % | ASTM D 955 |
Mold Shrinkage,flow,24 hrs(5) | 0.69 | % | ISO 294 |
Mold Shrinkage,xflow,24 hrs(5) | 1.7 | % | ISO 294 |
Density | 1.47 | g/cm³ | ISO 1183 |
ELECTRICAL | Value | Unit | Standard |
Surface Resistivity | 1.E+02-1.E+06 | Ohm | ASTM D 257 |
Source GMD,last updated:2010/12/16 |
Parameter Injection Molding | Value | Unit |
Drying Temperature | 80 | ℃ |
Drying Time | 4 | hrs |
Melt Temperature | 200-215 | ℃ |
Front-Zone 3 Temperature | 210-220 | ℃ |
Middle-Zone 2 Temperature | 195-205 | ℃ |
Rear-Zone 1 Temperature | 175-190 | ℃ |
Mold Temperature | 80-110 | ℃ |
Back Pressure | 0.2-0.3 | MPa |
Screw Speed | 30-60 | rpm |
Source GMD,last updated:2010/12/16 |