- 产 品：POM KE002 含有碳纤维.静态导电POM
- 产 地：美国液氮
- 价 格：电话报价
- 库 存：20吨
- 交 货：江苏苏州
- 苏州希普能：185 5121 3137 谭经理
LNP* STAT-KON* COMPOUND
LNP STAT-KON RESIN ALL SERIES
LNP* Stat-Kon* composites contain electrically conductive additives. They and span a broad range of surface resistivity and electrical activity, from antistatic, through conductive, to electromagnetic interference (EMI) shielding. Stat-Kon* composites offer cost-effective solutions when products must avoid static electricity buildup or discharge. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.
LNP™ STAT-KON™ Compound POM KE002 塑料物性表
Also known as:LNP™ Stat-kon™ Compound KC-1002 Product reorder name:KE002
LNP* Stat-Kon* KE002 is a compound based on Acetal resin containing Carbon Fiber. A characteristc of this grade is statically conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5mm/min | 1080 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5mm/min | 2.4 | % | ASTM D 638 |
| Flexural Stress,brk,1.3mm/min,50mm span | 1645580 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3mm/min,50mm span | 0 | kgf/cm² | ASTM D 790 |
| Tensile Stress,break,5mm/min | 104 | MPa | ISO 527 |
| Tensile Strain,break,5mm/min | 2 | % | ISO 527 |
| Tensile Modulus,1mm/min | 8220 | MPa | ISO 527 |
| Flexural Stress | 154 | MPa | ISO 178 |
| Flexural Modulus,2mm/min | 7050 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 38 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 4 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched 80*10*4 +23℃ | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 161 | ℃ | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.43 | - | ASTM D 792 |
| Mold Shrinkage,flow,24 hrs(5) | 0.5-0.7 | % | ASTM D 955 |
| Mold Shrinkage,xflow,24 hrs(5) | 1-3 | % | ASTM D 955 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02-1.E+05 | Ohm | ASTM D 257 |
| Source GMD,last updated:2011/12/14 | |||
| Parameter Injection Molding | Value | Unit |
| Drying Temperature | 80 | ℃ |
| Drying Time | 4 | hrs |
| Melt Temperature | 200-215 | ℃ |
| Front-Zone 3 Temperature | 210-220 | ℃ |
| Middle-Zone 2 Temperature | 195-205 | ℃ |
| Rear-Zone 1 Temperature | 175-190 | ℃ |
| Mold Temperature | 80-110 | ℃ |
| Back Pressure | 0.2-0.3 | MPa |
| Screw Speed | 30-60 | rpm |
| Source GMD,last updated:2011/12/14 | ||