POM KZL34 含磨碎的玻璃和聚四氟乙烯
  • 产 品:POM KZL34 含磨碎的玻璃和聚四氟乙烯
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP* Lubricomp* Compound
LNP Lubricomp Resin All Series
LNP* Lubricomp* compounds provide improved wear resistance and lower friction by combining engineering resins with internal lubricants. Lubricomp compounds, which can also be stiffened with glass or other fiber, can help extend product life and reduce or eliminate squeaks and other noise from moving parts. LNP specialty compound offerings are available in a broad portfolio of standard and engineering materials.

LNP™ Lubricomp™ Compound POM KZL34 塑料数据

Also known as:LNP™ Lubricomp™ Compound KFL-4034 M
Product reorder name:KZL34
LNP* Lubricomp* KZL34 is a compound based on Acetal resin containing Milled Glass and PTFE. Characteristic of this grade is Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 380 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 360 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 3.5 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 8 % ASTM D 638
Tensile Modulus,5mm/min 34200 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 730 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 29600 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 37 MPa ISO 527
Tensile Stress,break,5mm/min 34 MPa ISO 527
Tensile Strain,yield,5mm/min 3.5 % ISO 527
Tensile Strain,break,5mm/min 7 % ISO 527
Tensile Modulus,1mm/min 3220 MPa ISO 527
Flexural Stress 64 MPa ISO 178
Flexural Modulus,2mm/min 2960 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 35 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Multiaxial Impact 20 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 40 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 19 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 3 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 147 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 90 ASTM D 648
CTE,-30℃ to 30℃,flow 8.70E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 9.10E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 145 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 95 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.6 - ASTM D 792
Density 1.65 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.14 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 1-3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1-3 % ASTM D 955
Wear Factor Washer 160 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 5 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.43 - ASTM D 3702 Modified
Static COF 0.49 - ASTM D 3702 Modified
Moisture Absorption(23℃/50% RH) 0.22 % ISO 62
Source GMD,last updated:2011/02/08
Parameter Injection Molding Value Unit
Drying Temperature 65-75
Drying Time 4-6 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.01 %
Melt Temperature 220-250
Nozzle Temperature 220-250
Front-Zone 3 Temperature 220-250
Middle-Zone 2 Temperature 210-240
Rear-Zone 1 Temperature 180-220
Mold Temperature 40-60
Back Pressure 3-10 MPa
Screw Speed 30-80 rpm
Shot to Cylinder Size 30-70 %
Vent Depth 0.03-0.05 mm
Source GMD,last updated:2011/02/08

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

关健字:【LNP™ Lubricomp™ Compound POM KZL34