POM KL003 含有聚四氟乙烯,内部润滑
  • 产 品:POM KL003 含有聚四氟乙烯,内部润滑
  • 产 地:美国液氮
  • 价 格:电话报价
  • 库 存:20吨
  • 交 货:江苏苏州
  • 苏州希普能:185 5121 3137 谭经理

LNP Lubricomp* Acetal Compound
Bringing even more friction control to acetals
Acetal-based LNP Lubricomp compounds provide improved wear resistance and lower friction than unmodified base resins by combining acetals with internal lubricants. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound POM KL003 塑料物性

Also known as:LNP™ Lubricomp™ Compound KL-4030
Product reorder name:KL003
LNP LUBRICOMP* KL003 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated.

MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 480 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 480 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 10 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 19 % ASTM D 638
Tensile Modulus,50mm/min 25700 kgf/cm² ASTM D 638
Flexural Stress 770 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 22500 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 46 MPa ISO 527
Tensile Stress,break,5mm/min 46 MPa ISO 527
Tensile Strain,yield,5mm/min 9 % ISO 527
Tensile Strain,break,5mm/min 16 % ISO 527
Tensile Modulus,1mm/min 2460 MPa ISO 527
Flexural Modulus,2mm/min 2240 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 72 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 3 cm-kgf/cm ASTM D 256
Izod Impact,unnotched 80*10*4 +23℃ 45 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 3 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 158 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 97 ASTM D 648
CTE,-30℃ to 30℃,flow 1.07E-04 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 1.07E-04 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 149 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 88 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.49 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.2 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 1-3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1-3 % ASTM D 955
Wear Factor Washer 11 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Wear Factor Ring 0 10^-10 in^5-min/ft-lb-hr ASTM D 3702 Modified
Dynamic COF 0.35 - ASTM D 3702 Modified
Static COF 0.17 - ASTM D 3702 Modified
Density 1.49 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.29 % ISO 62
Source GMD,last updated:2008/12/18
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Melt Temperature 200-215
Front-Zone 3 Temperature 210-220
Middle-Zone 2 Temperature 195-205
Rear-Zone 1 Temperature 175-190
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2008/12/18

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.