LNP Lubricomp* Acetal Compound
Bringing even more friction control to acetals
Acetal-based LNP Lubricomp compounds provide improved wear resistance and lower friction than unmodified base resins by combining acetals with internal lubricants. Glass and carbon fibers can also be included for improved strength and stiffness.

LNP™ Lubricomp™ Compound POM KFL32R 塑料物性

Also known as:LNP™ Lubricomp™ Compound KFL-4032 ER
Product reorder name:KFL32R
LNP LUBRICOMP* KFL32R is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Easy Release.

MECHANICAL Value Unit Standard
Tensile Stress,break 810 kgf/cm² ASTM D 638
Tensile Strain,break 2.6 % ASTM D 638
Tensile Modulus,50mm/min 52000 kgf/cm² ASTM D 638
Flexural Stress 1180 kgf/cm² ASTM D 790
Flexural Modulus 49200 kgf/cm² ASTM D 790
Tensile Stress,break 79 MPa ISO 527
Tensile Strain,break 2.5 % ISO 527
Tensile Modulus,1mm/min 5400 MPa ISO 527
Flexural Stress 122 MPa ISO 178
Flexural Modulus 5800 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 35 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 4 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 69 cm-kgf ASTM D 3763
Multiaxial Impact 17 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 26 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 5 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 165 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 161 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 162 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.56 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.18 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 1.1 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1.3 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 1.08 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 1.34 % ISO 294
Density 1.56 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.33 % ISO 62
Source GMD,last updated:2004/09/29
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Melt Temperature 200-215
Front-Zone 3 Temperature 210-220
Middle-Zone 2 Temperature 195-205
Rear-Zone 1 Temperature 175-190
Mold Temperature 80-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2004/09/29

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 Buy SABIC Innovative please contact xiang zhang Engineering plastics

1、Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23℃/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
2、Only typical data for selection purposes. Not to be used for part or tool design.
3、This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
4、Internal measurements according to UL standards.
5、Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.